Idatha Yezobuchwepheshe
Ishidi lensimbi le-S235J0W I-Chemical analysis -% by mass*
| Amabanga |
C |
Si |
UMn |
P |
S |
Cu |
Cr |
Ni |
| ubuningi |
ubuningi |
ubuningi |
ubuningi |
ubuningi. |
ubuningi |
ubuningi |
ubuningi |
| I-S235 J0W |
0.13 |
0.4 |
0.20-1.66 |
0.035 |
0.035 |
0.25-0.55 |
0.40-0.80 |
0.65 |
| AmabangaS235 JOW |
Yield StrengthReH[N/mm2]transv.min |
I-TensileStrengthRm[N/mm2]transv |
I-FractureElongation[%]transv. imiz. |
I-Notch ImpactEnergy1)Ch V isampula ephelele yobude. iminithi [J] |
| e2) ≤ 16 |
e2)> 16 |
e2) <3 |
e2)≥3 |
e2) ≤ 2 |
e2) ≤ 2 |
|
| 235 |
225 |
360 kuya ku-510 |
360 kuya ku-510 |
19/17 |
20/18 |
- |
| EYurophu |
Werkst.-Nr. |
DE |
E-US |
I-Salzgitter Flachstahl |
FK1) |
| I-EN 10025-5 |
|
THENGA 087 |
I-ASTM |
|
|
| I-S235J0W |
1.8958 |
- |
- |
Allwesta 360 |
A |
| I-S235J2W |
1.8961 |
I-WTSt 37-3 |
- |
Allwesta 360 F |
A |
| I-S355J0WP |
1.8945 |
- |
- |
Allwesta 510 P |
B |
| I-S355J2WP |
1.8946 |
- |
A 242 Uhlobo 1 |
Allwesta 510 FP |
B |
| I-S355J0W |
1.8959 |
- |
awu 588 |
Allwesta 510 |
B |
| I-S355J2W |
1.8965 |
I-WTSt 52-3 |
- |
Allwesta 510 F |
B |
| I-S355K2W |
1.8967 |
- |
- |
I-Allwesta 510 F 40 |
B |
FK = Festigkeitsklasse, siehe Abmessungen
I-Chemische Zusammensetsung in Gewichtsprozent [%] (Schmelzenanalyse)
| Hlunga |
C |
Si |
UMn |
P |
S |
N |
Cr |
|
ubuningi. |
ubuningi. |
|
|
ubuningi. |
ubuningi. |
|
| I-S235J0W1) |
0,13 |
0,40 |
0,20 - 0,60 |
ubuningi. 0,035 |
0,035 |
0,0092) 3) |
0,40 - 0,80 |
| I-S235J2W1) |
0,13 |
0,40 |
0,20 - 0,60 |
ubuningi. 0,035 |
0,030 |
– 4) |
0,40 - 0,80 |
| I-S355J0WP1) |
0,12 |
0,75 |
ubuningi. 1,0 |
0,06 - 0,15 |
0,035 |
0,0093) |
0,30 - 1,25 |
| I-S355J2WP1) |
0,12 |
0,75 |
ubuningi. 1,0 |
0,06 - 0,15 |
0,030 |
– 4) |
0,30 - 1,25 |
| S355J0W1)5) |
0,16 |
0,50 |
0,50 - 1,50 |
ubuningi. 0,035 |
0,035 |
0,0092) 3) |
0,40 - 0,80 |
| S355J2W1)5) |
0,16 |
0,50 |
0,50 - 1,50 |
ubuningi. 0,030 |
0,030 |
– 4) |
0,40 - 0,80 |
| S355K2W1)5) |
0,16 |
0,50 |
0,50 - 1,50 |
ubuningi. 0,030 |
0,030 |
– 4) |
0,40 - 0,80 |
I-Die Stähle enthalten 0,25 bis 0,55% Cu und max. 0,65% Ni.
Eine Überschreitung des angegebenen Höchstwertes ist zulässig, wenn je 0,001% N ein um 0,005 % ngaphansi kwe-festgelegten Höchstwert liegender Phosphorgehalt eingehalten wird. Der Stickstoffgehalt beträgt jedoch höchstens 0,012 % in der Schmelzenanalyse.
Der Höchstwert für den Stickstoffgehalt gilt nicht, wenn die Stähle mindestens 0,020 % Altotal oder genügend Gehalte an anderen stickstoffabbindenden Elementen aufweisen.
Die Stähle enthalten mindestens eines der folgenden Elemente: Ingqikithi: ≥ 0,020 %, Nb: 0,015 - 0,060 %, V: 0,02 - 0,12%, Ti: 0,02 - 0,10 %. Wenn die Elemente in Kombination angewendet werden, ist mindestens eines von ihnen mit dem angegebenen Mindestgehalt enthalten.
I-Die Stähle dürfen max. 0,30 % Mo and max. 0,15 % Zr enthalten.
Mechanische Eigenschaften1)
| Hlunga |
I-Probenlage |
Okuncane. I-Streckgrenze2) [MPa] |
Zugfestigkeit2) [MPa] |
Okuncane. Bruchdehnung2) [%] |
|
|
|
|
|
|
L0 = 80 mm |
L0 = 5,65 √S0 |
|
|
e ≤16 |
e> 16 |
e <3 |
e ≥3 |
e≤2 |
2< e <2,5 |
2,5
| e ≥3 |
| I-S235J0W |
l/t |
235 |
225 |
360 - 510 |
360 - 510 |
19/17 |
20/18 |
21/19 |
26/24 |
| I-S235J2W |
l/t |
235 |
225 |
360 - 510 |
360 - 510 |
19/17 |
20/18 |
21/19 |
26/24 |
| I-S355J0WP |
l/t |
3553) |
- |
510 - 680 |
4703) - 6303) |
16/14 |
17/15 |
18/16 |
22/203) |
| I-S355J2WP |
l/t |
3553) |
- |
510 - 680 |
4703) - 6303) |
16/14 |
17/15 |
18/16 |
22/203) |
| I-S355J0W |
l/t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
| I-S355J2W |
l/t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
| I-S355K2W |
l/t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
Die in der Tabelle angegebenen Werte des Zugversuches gelten für Längsproben (I) außer bei Band und Blech ≥ 600 mm Breite, aus denen Querproben (t) zu entnehmen sind.
e = Nenndicke in mm
I-S355J0WP kanye ne-S355J2WP: e 12 ≤ mm
I-Kerbschlagarbeit im Lieferzustand (Mindestwerte an Charpy-V-Proben)
| Hlunga |
Izinga lokushisa [°C] |
I-Kerbschlagarbeit1) [J] |
|
|
|
| I-S235J0W |
0 |
27 |
| I-S235J2W |
-20 |
27 |
| I-S355J0WP |
0 |
27 |
| I-S355J2WP |
-20 |
27 |
| I-S355J0W |
0 |
27 |
| I-S355J2W |
-20 |
27 |
| I-S355K2W |
-20 |
40 |
I-Mittelwerte noma i-3 Proben; ein Einzelwert darf den geforderten Mindeswert um höchstens 30 % unterschreiten. Für Erzeugnisdicken von 6 - 10 mm entspricht die Probenbreite der jeweiligen Erzeugnisdicke, wobei die Prüfung an Charpy-V-ähnlichen Proben erfolgt. Die in der oberen Tabelle angegebenen Werte verringern sich hierbei proportional zur Probenbreite.
Isithombe se-Prinzip der Deckschicht
s355jow steel plate Properties
I-Chemical Properties Of s355jow Steel Plate
| Ibanga |
C |
Si |
UMn |
P |
S |
N |
Ukwengezwa kwe
ukubopha i-nitrogen
izakhi |
Cr |
Cu |
| I-S355J0W |
0.16 |
0.50 |
0.50/1.50 |
0.035 |
0.035 |
0.009 |
- |
0.40/0.80 |
0.25/0.55 |
| Ibanga |
Okuncane. Isivuno Amandla Reh MPa |
Amandla Aqinile Rm MPa |
| Ubukhulu Bezwi (mm) |
Ubukhulu Bezwi (mm) |
| ≤16 |
>16 ≤40 |
>40 ≤63 |
>63 ≤80 |
>80 ≤100 |
>100 ≤150 |
>3 |
>3 ≤100 |
>100 ≤150 |
| I-S355J0W |
355 |
345 |
335 |
325 |
315 |
295 |
510/680 |
470/630 |
450/600 |
| Okubalulekile # |
I-EN 10155 |
THENGA 087 |
I-NFA 35-502 |
I-UNI |
BS 4360 |
I-ASTM |
|
| 1.8961 |
I-S235J2W |
I-WTSt 37-3 |
E24 W4 |
Fe 360 DK 1 |
- |
- |
- |
| 1.8945 |
I-S355J0WP |
E36 WA 3 |
I-Fe 510 C1K1 |
I-WR50 A |
- |
- |
- |
| 1.8946 |
I-S355J2WP |
- |
E36 WA 4 |
I-Fe 510 D1K1 |
- |
A 242 Uhlobo 1 |
- |
| 1.8959 |
I-S355J0W |
- |
E36 WB 3 |
I-Fe 510 C2K1 |
I-WR50 B |
A 588 – A 242 Gr. 1 |
I-SMA 50 AW |
| 1.8963 |
I-S355J2G1W |
I-WTSt 52-3 |
- |
I-Fe 510 D2K1 |
I-WR 50 C |
awu 588g. A |
ku |
| 1.8965 |
I-S355J2G2W |
- |
- |
- |
- |
- |
I-SMA 50 CP |
| 1.8966 |
I-S355K2G1W |
- |
E36 WB 4 |
- |
- |
A 709 Gr. 50 W |
- |
| 1.8967 |
I-S355K2G2W |
- |
- |
- |
- |
- |
- |