C(M) | 0.95~1.05 | Si(%) | 0.15~0.35 | Mn(Mn) | 0.25~0.45 | P(M) | ≤0.025 |
S(M) | ≤0.025 | Kr(M) | 1.40~1.65 |
Awọn ohun-ini ẹrọ ti annealed GB GCr15 irin ti o nru (apẹrẹ fun irin) jẹ ilana ni tabili ni isalẹ:
Fifẹ | So eso | modulus olopobobo | Modulu rirẹ | Ipin Poisson | Gbona elekitiriki |
MPa | Mpa | Gpa | Gpa | W/mK | |
520 | 415 min | 140 | 80 | 0.27-0.30 | 46.6 |
Ooru itọju Jẹmọ
Laiyara kikan si 790-810 ℃ ati gba awọn akoko to, jẹ ki irin naa kikan daradara, Lẹhinna dara laiyara ninu ileru. Awọn ọna annealing ti o yatọ yoo gba oriṣiriṣi lile.GCr15 ti nmu irin yoo gba Hardness MAX 248 HB (Brinell hardness).
Kikan laiyara si 860°C, Lẹhinna pipaarẹ nipasẹ epo gba lile 62 si 66 HRc. Iwọn otutu otutu: 650-700 ℃, tutu ni afẹfẹ, gba lile 22 si 30HRC. Iwọn otutu kekere: 150-170 ℃, Tutu ni ari, gba lile 61-66HRC.
GB GCr15 irin le gbona ṣiṣẹ ni 205 si 538°C, GCr15 Irin ti o nru le jẹ iṣẹ tutu ni lilo awọn ilana aṣa ni annealed tabi awọn ipo deede.
GB GCr15 irin ti wa ni lilo pupọ fun ọpọlọpọ awọn ohun elo ni lilo si awọn bearings ni ẹrọ iyipo. Awọn ohun elo aṣoju gẹgẹbi awọn ara àtọwọdá, awọn ifasoke ati awọn ohun elo, fifuye giga ti kẹkẹ, awọn boluti, awọn boluti olori-meji, awọn jia, ẹrọ ijona inu. Awọn locomotives ina, awọn irinṣẹ ẹrọ, awọn tractors, ohun elo yiyi irin, ẹrọ alaidun, ọkọ oju-irin, ati ọpa gbigbe ẹrọ iwakusa lori bọọlu irin, rola ati apa ọpa, bbl