AISI 4140 Poʻlat ekvivalenti
| Mamlakat |
Xitoy |
Yaponiya |
Germaniya |
AQSH |
Britaniya |
| Standart |
GB/T 3077 |
JIS G4105 |
DIN (W-Nr.)
EN 10250 |
AISI/ASTM
ASTM A29 |
BS 970 |
| Baho |
42CrMo |
SCM440 |
42crmo4/1,7225 |
4140 |
EN19/709M40 |
AISI 4140 po'latning kimyoviy tarkibi
| Baho |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
| 42CrMo |
0.38-0.45 |
0.17-0.37 |
0.5-0.80 |
≤0,035 |
≤0,035 |
0.9-1.2 |
0.15-0.25 |
- |
| SCM440 |
0.38-0.43 |
0.15-0.35 |
0.6-0.85 |
≤0,035 |
≤0,04 |
0.9-1.2 |
0,15-0,30 |
- |
| 42crmo4/1,7225 |
0.38-0.45 |
≤ 0,4 |
0.6-0.9 |
≤0,025 |
≤0,035 |
0.9-1.2 |
0,15-0,30 |
- |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0,035 |
≤0,04 |
0.8-1.1 |
0,15-0,25 |
- |
| EN19/709M40 |
0.35-0.45 |
0.15-0.35 |
0.5-0.80 |
≤0,035 |
≤0,035 |
0.9-1.5 |
0.2-0.40 |
- |
AISI 4140 po'latning mexanik xususiyatlari (faqat yo'l-yo'riq uchun)
| Baho |
Mustahkamlik chegarasi
sb(MPa) |
Hosildorlik kuchi
s (MPa) |
Cho'zilish
d5 (%) |
Kamaytirish
ps (%) |
Ta'sir qiymati
Akv (J) |
Qattiqlik |
| 4140 |
≥1080 |
≥930 |
≥12 |
≥45 |
≥63 |
28-32 HRC |
AISI 4140 po'lat haqida umumiy ma'lumot
| Hajmi |
Dumaloq |
Diametri 6-1200 mm |
| Plitalar/Yassi/Blok |
Qalinligi
6 mm - 500 mm |
Kengligi
20 mm - 1000 mm |
| Issiqlik bilan ishlov berish |
Normallashtirilgan; Tavlangan; Söndürülmüş; Jahldor |
| Yuzaki holati |
Qora; tozalangan; sayqallangan; Qayta ishlangan; Maydalangan; aylantirildi; Tegirmonlangan |
| Yetkazib berish sharti |
Soxta; Issiq haddelenmiş; Sovuq chizilgan |
| Sinov |
Kuchlanish kuchi, rentabellik kuchi, cho'zilish, pasayish maydoni, zarba qiymati, qattiqlik, don o'lchami, ultratovush tekshiruvi, AQSh tekshiruvi, magnit zarrachalar sinovi va boshqalar. |
| To'lov shartlari |
T/T;L/C;/Money gramm/ Paypal |
| Savdo shartlari |
FOB; CIF; C&F; va boshqalar.. |
| Yetkazib berish vaqti |
30-45 kun |
| Ilova |
AISI 4140 po'lati aerokosmik, neft va gaz, avtomobilsozlik, qishloq xo'jaligi va mudofaa sanoati uchun zarb qilish uchun ko'plab ilovalarni topadi.
4140 po'latdan foydalanish uchun odatiy dasturlarga quyidagilar kiradi: zarb qilingan tishli g'ildiraklar, shpindellar, armatura, jiglar, bo'yinbog'lar, o'qlar, konveyer qismlari, qarg'alar, yog'och qismlar, vallar, tishli vintlar, tirgaklar, pinionlar, nasos vallari, qo'chqorlar va halqali tishli va boshqalar. |
Jismoniy xususiyatlar
AISI 4140 qotishma po'latining jismoniy xususiyatlari quyidagi jadvalda ta'kidlangan.
| Xususiyatlari |
Metrik |
Imperator |
| Zichlik |
7,85 g/sm3 |
0,284 funt/in³ |
| Erish nuqtasi |
1416 ° S |
2580° F |
Mexanik xususiyatlar
Quyidagi jadvalda AISI 4140 qotishma po'latning mexanik xususiyatlari ko'rsatilgan.
| Xususiyatlari |
Metrik |
Imperator |
| Mustahkamlik chegarasi |
655 MPa |
95000 psi |
| Hosildorlik kuchi |
415 MPa |
60200 psi |
| Ommaviy modul (po'lat uchun odatiy) |
140 GPa |
20300 ksi |
| Kesish moduli (po'lat uchun odatiy) |
80 GPa |
11600 ksi |
| Elastik modul |
190-210 GPa |
27557-30458 ksi |
| Puasson nisbati |
0.27-0.30 |
0.27-0.30 |
| Uzilish cho'zilishi (50 mm da) |
25.70% |
25.70% |
| Qattiqlik, Brinell |
197 |
197 |
| Qattiqlik, Knoop (Brinell qattiqligidan aylantirilgan) |
219 |
219 |
| Qattiqlik, Rokvell B (Brinell qattiqligidan aylantirilgan) |
92 |
92 |
| Qattiqlik, Rokvell C (Brinell qattiqligidan aylantirilgan. Qiymat oddiy HRC diapazonidan past, faqat taqqoslash uchun) |
13 |
13 |
| Qattiqlik, Vikers (Brinell qattiqligidan aylantirilgan) |
207 |
207 |
| Ishlov berish qobiliyati (AISI 1212 asosida 100 ishlov berish imkoniyati sifatida) |
65 |
65 |
Issiqlik xususiyatlari
AISI 4140 qotishma po'latning issiqlik xususiyatlari quyidagi jadvalda keltirilgan.
| Xususiyatlari |
Metrik |
Imperator |
| Issiqlik kengayish koeffitsienti (@ 0-100°C/32-212°F) |
12,2 mkm/m°C |
6,78 mikron/in°F |
| Issiqlik o'tkazuvchanligi (@ 100 ° C) |
42,6 Vt/mK |
296 BTU in/hr.ft².°F |
Boshqa belgilar
AISI 4140 qotishma po'latiga teng keladigan boshqa belgilar quyidagi jadvalda keltirilgan.
| AMS 6349 |
ASTM A193 (B7, B7M) |
ASTM A506 (4140) |
ASTM A752 (4140) |
| AMS 6381 |
ASTM A194 (7, 7M) |
ASTM A513 |
ASTM A829 |
| AMS 6382 |
ASTM A29 (4140) |
ASTM A513 (4140) |
SAE J1397 (4140) |
| AMS 6390 |
ASTM A320 (L7, L7M, L7D) |
ASTM A519 (4140) |
SAE J404 (4140) |
| AMS 6395 |
ASTM A322 (4140) |
ASTM A646 (4140) |
SAE J412 (4140) |
| AMS 6529 |
ASTM A331 (4140) |
ASTM A711 |
|
Ishlab chiqarish va issiqlik bilan ishlov berish
Ishlov berish qobiliyati
AISI 4140 qotishma po'lati tavlangan holatda yaxshi ishlov berish qobiliyatiga ega.
Shakllantirish
AISI 4140 qotishma po'lati yuqori egiluvchanlikka ega. U tavlangan holatda an'anaviy texnikalar yordamida shakllantirilishi mumkin. U shakllantirish uchun ko'proq bosim yoki kuch talab qiladi, chunki u oddiy karbonli po'latlarga qaraganda qattiqroq.
Payvandlash
AISI 4140 qotishma po'latni barcha an'anaviy texnikalar yordamida payvandlash mumkin. Biroq, bu po'latning mexanik xususiyatlari issiqlik bilan ishlov berilgan holatda payvandlangan bo'lsa, ta'sir qiladi va payvandlashdan keyingi issiqlik bilan ishlov berish kerak.
Issiqlik bilan ishlov berish
AISI 4140 qotishma po'lat 845 ° C (1550 ° F) da isitiladi, keyin yog'da so'ndiriladi. Qattiqlashuvdan oldin uni uzoq vaqt davomida 913 ° C (1675 ° F) haroratda isitish, keyin havo sovutish orqali normalizatsiya qilish mumkin.
Soxtalashtirish
AISI 4140 qotishma po'lat 926 dan 1205 ° C gacha (1700 dan 2200 ° F gacha) zarb qilingan.
Issiq ishlash
AISI 4140 qotishma po'latdan 816 dan 1038 ° C gacha (1500 dan 1900 ° F gacha) issiq ishlov berilishi mumkin.
Sovuq ishlash
AISI 4140 qotishma po'latni an'anaviy usullar yordamida tavlangan holatda sovuq ishlov berish mumkin.
Yuvish
AISI 4140 qotishma po'lat 872 ° C (1600 ° F) da tavlanadi, so'ngra o'choqda sekin soviydi.
Temperlash
AISI 4140 qotishma po'latni kerakli qattiqlik darajasiga qarab 205 dan 649 ° C gacha (400 dan 1200 ° F) haroratda ishlov berish mumkin. Po'latning qattiqligi, agar u pastroq haroratga ega bo'lsa, oshirilishi mumkin. Misol uchun, 225 ksi kuchlanish kuchiga 316 ° C (600 ° F) da ishlov berish orqali erishish mumkin va 130 ksi valentlik kuchiga 538 ° C (1000 ° F) da ishlov berish orqali erishish mumkin.
Qattiqlashuv
AISI 4140 qotishma po'lat sovuq ishlov berish yoki isitish va söndürme orqali qattiqlashishi mumkin.