Tehniki maglumatlar
AISI 4140 Polat ekwiwalenti
| Countryurt |
Hytaý |
Japanaponiýa |
Germaniýa |
ABŞ |
Iňlisler |
| Standart |
GB / T 3077 |
JIS G4105 |
DIN (W-Nr.)
EN 10250 |
AISI / ASTM
ASTM A29 |
BS 970 |
| Baha |
42CrMo |
SCM440 |
42crmo4 / 1.7225 |
4140 |
EN19 / 709M40 |
AISI 4140 polat himiki düzümi
| Baha |
C. |
Si |
Mn |
S. |
S. |
Cr |
Mo. |
Ni |
| 42CrMo |
0.38-0.45 |
0.17-0.37 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.2 |
0.15-0.25 |
- |
| SCM440 |
0.38-0.43 |
0.15-0.35 |
0.6-0.85 |
≤0.035 |
≤0.04 |
0.9-1.2 |
0.15-0.30 |
- |
| 42crmo4 / 1.7225 |
0.38-0.45 |
≤ 0.4 |
0.6-0.9 |
≤0.025 |
≤0.035 |
0.9-1.2 |
0.15-0.30 |
- |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0.035 |
≤0.04 |
0.8-1.1 |
0.15-0.25 |
- |
| EN19 / 709M40 |
0.35-0.45 |
0.15-0.35 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.5 |
0.2-0.40 |
- |
AISI 4140 polat mehaniki aýratynlyklary (diňe ýol görkezmek üçin)
| Baha |
Dartyş güýji
σb (MPa) |
Hasyl beriň
σs (MPa) |
Uzalma
δ5 (%) |
Azaltmak
ψ (%) |
Täsiriň gymmaty
Akv (J) |
Gatylyk |
| 4140 |
801080 |
30930 |
≥12 |
≥45 |
≥63 |
28-32HRC |
AISI 4140 polat syn
| Ölçegi |
Tegelek |
Dia 6-1200mm |
| Tabak / Tekiz / Blok |
Galyňlyk
6mm-500mm |
Ini
20mm-1000mm |
| Atylylyk bejergisi |
Kadalaşdyrylan; Baglanan; Öçürilen; Tempered |
| Faceerüsti ýagdaý |
Gara; Peel; Jaýlanan; Işlenen; Taşlanan; Öwrüldi; Milled |
| Eltip bermek ýagdaýy |
Galp; Gyzgyn rulon; Sowuk çekildi |
| Synag |
Dartyş güýji, hasyl güýji, uzalmagy, peselýän ýeri, täsir gymmaty, gatylygy, däne ululygy, ultrases barlagy, ABŞ barlagy, magnit bölejikleri barlamak we ş.m. |
| Tölegiň şerti |
T / T; L / C; / Pul gramy / Paypal |
| Söwda şertleri |
FOB; CIF; C&F; we ş.m. |
| Eltip bermegiň wagty |
30-45 gün |
| Arza |
AISI 4140 polat howa, nebit we gaz, awtoulag, oba hojalygy we goranyş pudaklary we ş.m.
4140 polatdan peýdalanmak üçin adaty programmalar şulary öz içine alýar: ýasalan dişli enjamlar, pyçaklar, armatura, jigler, ýakalar, oklar, konweýer bölekleri, garga barlary, agaç bölekleri, şahlar, pyçaklar, taýaklar, çeňňekler, nasos şahlary, goçlar we halka dişli we ş.m. |
Fiziki aýratynlyklar
AISI 4140 garyndy poladyň fiziki aýratynlyklary aşakdaky tablisada görkezilýär.
| Sypatlar |
Metrik |
Imperial |
| Dykyzlygy |
7,85 g / cm3 |
0.284 funt / in³ |
| Ereýän nokat |
1416 ° C. |
2580 ° F. |
Mehaniki aýratynlyklary
Aşakdaky tablisada AISI 4140 garyndy poladyň mehaniki aýratynlyklary görkezilýär.
| Sypatlar |
Metrik |
Imperial |
| Dartyş güýji |
655 MPa |
95000 psi |
| Hasyl beriň |
415 MPa |
60200 psi |
| Köp modul (polat üçin adaty) |
140 GPa |
20300 ksi |
| Gyrkym moduly (polat üçin adaty) |
80 GPa |
11600 ksi |
| Elastik modul |
190-210 GPa |
27557-30458 ksi |
| Poissonyň gatnaşygy |
0.27-0.30 |
0.27-0.30 |
| Arakesmede uzalma (50 mm) |
25.70% |
25.70% |
| Gatylyk, Brinell |
197 |
197 |
| Gatylyk, Knoop (Brinelliň gatylygyndan üýtgedildi) |
219 |
219 |
| Gatylyk, Rokwell B (Brinelliň gatylygyndan üýtgedildi) |
92 |
92 |
| Gatylyk, Rokwell C (Brinelliň gatylygyndan üýtgedildi. Adaty HRC diapazonyndan pes baha, diňe deňeşdirmek üçin) |
13 |
13 |
| Gatylyk, Wikers (Brinelliň gatylygyndan üýtgedildi) |
207 |
207 |
| Maşynlylyk (AISI 1212-iň 100 işleýşi hökmünde) |
65 |
65 |
Malylylyk aýratynlyklary
AISI 4140 garyndy poladyň ýylylyk aýratynlyklary aşakdaky tablisada berilýär.
| Sypatlar |
Metrik |
Imperial |
| Malylylyk giňelme koeffisiýenti (@ 0-100 ° C / 32-212 ° F) |
12.2 µm / m ° C. |
6.78 µin / ° F. |
| Malylylyk geçirijiligi (@ 100 ° C) |
42,6 W / mK |
296 BTU / sagatda. ° F. |
Beýleki bellikler
AISI 4140 garyndy polatyna deň bolan beýleki bellikler aşakdaky tablisada görkezilýär.
| AMS 6349 |
ASTM A193 (B7, B7M) |
ASTM A506 (4140) |
ASTM A752 (4140) |
| AMS 6381 |
ASTM A194 (7, 7M) |
ASTM A513 |
ASTM A829 |
| AMS 6382 |
ASTM A29 (4140) |
ASTM A513 (4140) |
SAE J1397 (4140) |
| AMS 6390 |
ASTM A320 (L7, L7M, L7D) |
ASTM A519 (4140) |
SAE J404 (4140) |
| AMS 6395 |
ASTM A322 (4140) |
ASTM A646 (4140) |
SAE J412 (4140) |
| AMS 6529 |
ASTM A331 (4140) |
ASTM A711 |
|
Önümçilik we ýylylygy bejermek
Ussatlyk
AISI 4140 garyndy polatdan ýasalan ýagdaýynda oňat işleýşi bar.
Formasiýa
AISI 4140 garyndy poladyň ýokary süýümliligi bar. Anörite şertlerde adaty usullary ulanyp emele gelip biler. Formingönekeý uglerod çeliklerinden has berk bolany üçin emele gelmek üçin has köp basyş ýa-da güýç talap edýär.
Kebşirlemek
AISI 4140 garyndy polat ähli adaty usullary ulanyp kebşirläp bolýar. Şeýle-de bolsa, bu poladyň mehaniki aýratynlyklary ýylylyk bilen bejerilen ýagdaýynda kebşirlense täsir eder we kebşeden soňky ýylylyk bejergisi geçirilmelidir.
Atylylygy bejermek
AISI 4140 garyndy polat 845 ° C (1550 ° F) bilen gyzdyrylýar, soňra ýagda söndürilýär. Gatylaşmazdan ozal, ony 913 ° C (1675 ° F) uzak wagtlap gyzdyryp, soňra howa sowadyp kadalaşdyryp bolýar.
Galplyk
AISI 4140 garyndy polat 926 - 1205 ° C (1700 - 2200 ° F) aralygynda ýasalýar
Gyzgyn iş
AISI 4140 garyndy polat 816-dan 1038 ° C (1500-den 1900 ° F) çenli gyzdyrylyp bilner.
Sowuk işlemek
AISI 4140 garyndy polat, adaty ýagdaýda adaty usullar bilen sowuk işlenip bilner.
Annealing
AISI 4140 garyndy polat 872 ° C (1600 ° F) bilen ýakylýar we ojakda ýuwaş-ýuwaşdan sowadylýar.
Tempering
AISI 4140 garyndy polat, islenýän gatylyk derejesine baglylykda 205-den 649 ° C (400-den 1200 ° F) çenli gyzdyrylyp bilner. Poladyň gatylygy, has pes temperatura bolsa, ýokarlanyp biler. Mysal üçin, 315 ° C (600 ° F) temperaturada 225 ksi dartyş güýjüne, 538 ° C (1000 ° F) temperaturada 130 ksi dartyş güýjüne ýetip bolýar.
Gatylaşdyrmak
AISI 4140 garyndy polat sowuk işlemek ýa-da ýylatmak we söndürmek arkaly gatylaşdyrylyp bilner.