Tehniki maglumatlar
S235J0W polat list Himiki derňew - köpçülik boýunça% *
| Bahalar |
C. |
Si |
Mn |
S. |
S. |
Cu |
Cr |
Ni |
| iň ýokary |
iň ýokary |
iň ýokary |
iň ýokary |
iň ýokary |
iň ýokary |
iň ýokary |
iň ýokary |
| S235 J0W |
0.13 |
0.4 |
0.20-1.66 |
0.035 |
0.035 |
0.25-0.55 |
0.40-0.80 |
0.65 |
| GradesS235 JOW |
Hasyl güýjiReH [N / mm2] transv.min |
TensileStrengthRm [N / mm2] transw |
Döwük uzynlygy [%] transv. min. |
Notch ImpactEnergy1) Ch Wcomplete samplelongitud. min [J] |
| e2) ≤ 16 |
e2)> 16 |
e2) <3 |
e2) ≥3 |
e2) ≤ 2 |
e2) ≤ 2 |
|
| 235 |
225 |
360-dan 510-a çenli |
360-dan 510-a çenli |
19 / 17 |
20/18 |
- |
| Europaewropa |
Werkst.-Nr. |
DE |
ABŞ |
Salzgitter Flachstahl |
FK1) |
| EN 10025-5 |
|
087 tikiň |
ASTM |
|
|
| S235J0W |
1.8958 |
- |
- |
Allwesta 360 |
A. |
| S235J2W |
1.8961 |
WTSt 37-3 |
- |
Allwesta 360 F. |
A. |
| S355J0WP |
1.8945 |
- |
- |
Allwesta 510 P. |
B. |
| S355J2WP |
1.8946 |
- |
242 görnüş 1 |
Allwesta 510 FP |
B. |
| S355J0W |
1.8959 |
- |
A 588 |
Allwesta 510 |
B. |
| S355J2W |
1.8965 |
WTSt 52-3 |
- |
Allwesta 510 F. |
B. |
| S355K2W |
1.8967 |
- |
- |
Allwesta 510 F 40 |
B. |
FK = Festigkeitsklasse, Abmessungen
Gewichtsprozentdäki Chemische Zusammensetzung [%] (Schmelzenanalyse)
| Sorte |
C. |
Si |
Mn |
S. |
S. |
N. |
Cr |
|
iň ýokary |
iň ýokary |
|
|
iň ýokary |
iň ýokary |
|
| S235J0W1) |
0,13 |
0,40 |
0,20 - 0,60 |
iň ýokary 0,035 |
0,035 |
0,0092) 3) |
0,40 - 0,80 |
| S235J2W1) |
0,13 |
0,40 |
0,20 - 0,60 |
iň ýokary 0,035 |
0,030 |
- 4) |
0,40 - 0,80 |
| S355J0WP1) |
0,12 |
0,75 |
iň ýokary 1,0 |
0,06 - 0,15 |
0,035 |
0,0093) |
0,30 - 1,25 |
| S355J2WP1) |
0,12 |
0,75 |
iň ýokary 1,0 |
0,06 - 0,15 |
0,030 |
- 4) |
0,30 - 1,25 |
| S355J0W1) 5) |
0,16 |
0,50 |
0,50 - 1,50 |
iň ýokary 0,035 |
0,035 |
0,0092) 3) |
0,40 - 0,80 |
| S355J2W1) 5) |
0,16 |
0,50 |
0,50 - 1,50 |
iň ýokary 0,030 |
0,030 |
- 4) |
0,40 - 0,80 |
| S355K2W1) 5) |
0,16 |
0,50 |
0,50 - 1,50 |
iň ýokary 0,030 |
0,030 |
- 4) |
0,40 - 0,80 |
Die Stähle 0,25 bis 0,55% Cu und max. 0,65% Ni.
Eine Überschreitung des angegebenen Höchstwertes is zulässig, wenn je 0,001% N ein um 0,005% unter dem festgelegten Höchstwert legender Fosforgehalt eingehalten wird. Der Şmelzenanalyse der Stickstoffgehalt beträgt jedoch höchstens 0,012%.
Der Höchstwert für den Stickstoffgehalt gilt nicht, wenn die Stähle 0,020% Altotal oder genügend Gehalte we anderen stickstoffabbindenden Elementen aufweisen.
Die Stähle enthalten mindestens eines der folgenden Elemente: Altotal: ≥ 0,020%, Nb: 0,015 - 0,060%, V: 0,02 - 0,12%, Ti: 0,02 - 0,10%. Womb Die Elemente, “Kombination angewendet werden”, “Mindestgehalt enthalten” -iň pikirini ýitirýär.
Die Stähle dürfen max. 0,30% Mo we iň ýokary. 0,15% Zr entalten.
Mehanische Eigenschaften1)
| Sorte |
Probenlage |
Min. Streckgrenze2) [MPa] |
Zugfestigkeit2) [MPa] |
Min. Bruchdehnung2) [%] |
|
|
|
|
|
|
L0 = 80 mm |
L0 = 5,65 √S0 |
|
|
e ≤ 16 |
e> 16 |
e <3 |
e ≥ 3 |
e≤2 |
2
| 2,5
| e ≥ 3 |
| S235J0W |
l / t |
235 |
225 |
360 - 510 |
360 - 510 |
19/17 |
20/18 |
21/19 |
26/24 |
| S235J2W |
l / t |
235 |
225 |
360 - 510 |
360 - 510 |
19/17 |
20/18 |
21/19 |
26/24 |
| S355J0WP |
l / t |
3553) |
- |
510 - 680 |
4703) - 6303) |
16/14 |
17/15 |
18/16 |
22/203) |
| S355J2WP |
l / t |
3553) |
- |
510 - 680 |
4703) - 6303) |
16/14 |
17/15 |
18/16 |
22/203) |
| S355J0W |
l / t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
| S355J2W |
l / t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
| S355K2W |
l / t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
Der Tabelle angegebenen Werte des Zugversuches gelten für Längsproben (I) außer bei Band und Blech ≥ 600 mm Breite, Querproben (t) zu entnehmen sind.
e = Nenndicke mm
S355J0WP und S355J2WP: e 12 ≤ mm
Kerbschlagarbeit im Lieferzustand (Mindestwerte Charpy-V-Proben)
| Sorte |
Temperatura [° C] |
Kerbschlagarbeit1) [J] |
|
|
|
| S235J0W |
0 |
27 |
| S235J2W |
-20 |
27 |
| S355J0WP |
0 |
27 |
| S355J2WP |
-20 |
27 |
| S355J0W |
0 |
27 |
| S355J2W |
-20 |
27 |
| S355K2W |
-20 |
40 |
Mittelwerte aus 3 Proben; ein Einzelwert darf den geforderten Mindestwert um höchstens 30% unterschreiten. Für Erzeugnisdicken von 6 - 10 mm entspricht die Probenbreite der jeweiligen Erzeugnisdicke, wobei die Prüfung Charpy-V-ähnlichen Proben erfolgt. Der oberen Tabelle angegebenen Werte verringern sich hierbei proporsional zur Probenbreite.
Prinzip der Deckschichtbildung
s355jow polat plastinka Sypatlar
S355jow polat plastinanyň himiki aýratynlyklary
| Baha |
C. |
Si |
Mn |
S. |
S. |
N. |
Goşmak
azot baglaýjy
elementleri |
Cr |
Cu |
| S355J0W |
0.16 |
0.50 |
0.50/1.50 |
0.035 |
0.035 |
0.009 |
- |
0.40/0.80 |
0.25/0.55 |
| Baha |
Min. Hasyl bermegiň güýji Reh MPa |
Dartyş güýji Rm MPa |
| Nominal galyňlyk (mm) |
Nominal galyňlyk (mm) |
| ≤16 |
> 16 ≤40 |
> 40 ≤63 |
> 63 ≤80 |
> 80 ≤100 |
> 100 ≤150 |
> 3 |
> 3 ≤100 |
> 100 ≤150 |
| S355J0W |
355 |
345 |
335 |
325 |
315 |
295 |
510/680 |
470/630 |
450/600 |
| Material # |
EN 10155 |
087 tikiň |
NFA 35-502 |
UNI |
BS 4360 |
ASTM |
|
| 1.8961 |
S235J2W |
WTSt 37-3 |
E 24 W 4 |
Fe 360 DK 1 |
- |
- |
- |
| 1.8945 |
S355J0WP |
E 36 WA 3 |
Fe 510 C1K1 |
WR 50 A. |
- |
- |
- |
| 1.8946 |
S355J2WP |
- |
E 36 WA 4 |
Fe 510 D1K1 |
- |
242 görnüş 1 |
- |
| 1.8959 |
S355J0W |
- |
E 36 WB 3 |
Fe 510 C2K1 |
WR 50 B. |
A 588 - A 242 Gr. 1 |
SMA 50 AW |
| 1.8963 |
S355J2G1W |
WTSt 52-3 |
- |
Fe 510 D2K1 |
WR 50 C. |
588 Gr. A. |
to |
| 1.8965 |
S355J2G2W |
- |
- |
- |
- |
- |
SMA 50 CP |
| 1.8966 |
S355K2G1W |
- |
E 36 WB 4 |
- |
- |
A 709 Gr. 50 Wt |
- |
| 1.8967 |
S355K2G2W |
- |
- |
- |
- |
- |
- |