Kelas baja: S890Q/S890QL/S890QL1. Standar palaksanaan: BS EN10025-04
Ukuran: 5 ~ 300 mm x 1500-4500 mm x L
| Bahan | Kualitas | C | Bungbulang | Si | P | S |
| S890Q/S890QL/S890QL1 HSLA plat baja | / | ≤0.20 | ≤1.70 | ≤0.80 | ≤0,025 | ≤0,015 |
| L | ≤0,020 | ≤0,010 | ||||
| L1 | ≤0,020 | ≤0,010 |
| Bahan | Kakuatan ngahasilkeun σ0,2 MPa | Kakuatan tarik σb MPa | Elongationδ5 % | V Pangaruh Manjang |
||
| ≥6-50 | ＞50-100 | ≥6 -50 | ＞50-100 | |||
| S890Q | ≥890 | ≥870 | 900-1060 | ≥13 | -20 ℃ ≥30J | |
| S890QL | -40 ℃ ≥30J | |||||
| S890QL1 | -60 ℃ ≥30J | |||||
S890QL Quenched na Tempered Struktural Steel
Panas-ngabentuk
Panas-ngabentuk luhur 580 ° C mungkin. A quenching salajengna jeung tempering kudu dilaksanakeun nurutkeun kaayaan pangiriman.
Panggilingan
Pangeboran kalawan kobalt-alloyed steels speed tinggi HSSCO. Laju motong kedah kirang langkung 17 - 19 m/min. Upami latihan HSS dianggo, laju motong kedah kirang langkung 3 - 5 m /mnt.
Seuneu-Motong
Suhu bahan kedah sahenteuna RT pikeun motong seuneu. Sajaba ti éta, hawa preheating handap disarankeun pikeun ketebalan plat tangtu: Pikeun ketebalan plat leuwih 40mm, preheat ka 100 ° C jeung ketebalan leuwih 80mm, preheat ka 150 ° C.
Las
S890QL baja cocog pikeun sakabéh métode las ayeuna. Suhu bahan kedah sahenteuna RT pikeun las. Sajaba ti éta, suhu preheating handap dianjurkeun pikeun ketebalan plat tangtu:
20mm – 40mm: 75°C
Leuwih 40mm: 100°C
60mm tur leuwih: 150°C
Indikasi ieu ngan ukur nilai standar, prinsipna, indikasi SEW 088 kedah dipatuhi.
The t 8 / 5 kali kedah antara 5 jeung 25 s, gumantung kana téhnik las dipaké. Upami annealing ngaleungitkeun setrés dipikabutuh pikeun alesan konstruksi, ieu kedah dilakukeun dina kisaran suhu 530 ° C-580 ° C.