Letlapa la tšepe la WSTE500

Ho latela EN 10025-2, poleiti ea tšepe ea S275J2 e sebelisoa haholo indastering ea kaho le boenjineri ba mechini, lijana, litanka le li-profiles tsa tšepe tse kolobisitsoeng joalo ka tšepe ea angle, sebopeho sa tšepe, H-beam, T-section. Bakeng sa tšepe ea carbon ea S275J2, haeba bareki ba batla ho ntlafatsa ts'ebetso ea tšepe ha ba sebelisa, baenjiniere ba rona ba ntse ba khothalletsa ho tloaeleha ho phekola mocheso. Ho seng joalo, tšepe e tlameha ho etsa tlhahlobo ea mocheso o tlase ho -20 ° C.

DIN WStE500 poleiti ea tšepe, ha e le sebopeho sa lik'hemik'hale, litaba tse fapaneng li fumaneha haholo ka har'a khabone, athe khabone e le A283Gr. d ha e fete 0.27%, mme e phahame ho feta grade C (≤0.24%); Ha e le thepa ea mochine, phapang e teng ka matla a ho tsitsa le ho fana ka matla, ha ASTM A283 Gr.D e na le matla a maholo a 415-550MPa (60-80 ksi) le ASTM A283 D grade e na le matla a 230MPa (33 ksi). ).

Kereiti	C ≤	Si	Mong	P ≤	S ≤	N ≤	Al ≥	Kr ≤	Cu ≤	Mo ≤	Ni ≤	Nb ≤	Ti ≤	V ≤	Nb+Ti+V ≤
WStE500	0.21	0.10~0.60	1.00~1.70	0.035	0.030	0.020	0.020	0.30	0.20	0.10	1.00	0.05	---	0.22	0.22

Mephato

Tensile Strength Rm bakeng sa botenya ba sehlahisoa s, ka mm N/mm²

UpperYield StressReH²) bakeng sa botenya ba sehlahisoa s, ka mm N/mm² min.

Elongation ka mor'a ho robeha3) (Lo=5do) % mets.

Mandrel bophara bakeng sa teko ea bend 4), 5)

s≤70

70＜s≤85

85＜s≤100

100＜s≤125

125＜s≤150

s≤16

16＜s≤35

35＜s≤50

50＜s≤60

60＜s≤70

70＜s≤85

85＜s≤100

100＜s≤125

125＜s≤150

Longitudinal

Transverse 6)

WStE500

610~780

600~770

590~760

580~750

570~740

500

480

470

460

450

440

430

420

410

16