ASTM A537 cl3 Alloy Pressure Vessel saxan bir ah

A537CL3 waa la dabcay oo la demiyay silikoon kaarboon manganese birta ah oo loogu talagalay ujeedooyin kala duwan. Shuruudaha ayaa muujinaya tijaabinta iyo sidoo kale habka iyo hababka u adkeysiga. Waxa kale oo ka mid ah kala duwanaanshaha cabbirka, hagaajinta cillad kasta, tirada, cufnaanta, rarista, calaamadaynta, baakadaha iwm. Gnee waxay si buuxda ugu lug leedahay bixinta tayada ugu wanaagsan ee suurtogalka ah ee alaabta. Warshadaha ayaa dammaanad qaadaya in ay si wax ku ool ah u fuliyaan dhammaan dalabaadka iibsadaha. Markaa waxay soo saarayaan taarikada iyagoo isticmaalaya tayada ugu sareysa ee daawaynta oo lagu daro tignoolajiyada ugu dambeeyay iyo aaladaha casriga ah. Sidoo kale, waxay tixgalinayaan hab-raaca wax-soo-saarka warshadaha iyo heerarka tayada alaabta ceeriin ee kala duwan ee soo saarista alaabta.

A537 fasalka 3  Halabuurka Kiimikada
Darajo	Cunsurka ugu sarreeya (%)
	C	Mn	P	S	Si	Cu	Ni	Cr	Mo
A537 fasalka 3	0.24	0.92-1.72	0.035	0.035	0.13-0.55	0.38	0.28	0.29	0.09

Darajo	A537 fasalka 3  Hantida makaanikada
	Dhumucda	Wax-soo-saarka	Jilicsan	Dheeraynta
A537 fasalka 3	mm	Min Mpa	Mpa	Ugu yaraan %
	-65	380	550-690	22
	65-100	345	515-655	20
	100-150	275	485-620	-

Dukumentiyada tixraaca

Heerarka ASTM:

A20/A20M: Faahfaahinta Shuruudaha Guud ee Taarikada Weelka Cadaadiska
A435 /A435: Loogu talagalay Baaritaanka Tooska ah ee Ultrasonic ee Saxanka Birta
A577/A577M: Loogu talagalay Imtixaanka Xagalka Ultrasonic-Beam ee Taarikada Birta
A578/A578M: ​​Si Toosan-Beam Baaritaanka Ultrasonic ee Taarikada Birta La Dulmaray ee Codsiyada Gaarka ah

Qoraallada wax-soo-saarka:

Birta birta ee hoos timaada ASTM A537 Class 1, 2 iyo 3 waa in la dilo birta oo u hoggaansama shuruudaha cabbirka hadhuudhka austenitic ee Qeexida A20 / A20M.

Hababka Daawaynta Kulaylka:

Dhammaan taarikada hoos timaada ASTM A537 waa in kulaylka loola dhaqmaa sida soo socota:
Taarikada ASTM A537 Class 1 waa in la caadiyeeyaa.
Fasalka 2 iyo fasalka 3 waa in la demiyo oo la dabciyaa. Heerkulka heerkulbeegga ee taarikada 2 waa in aanu ka yarayn 1100°F [595°C] oo aanu ka yarayn 1150°F [620°C] ee darajada 3aad.