Alloy 310 o se austenitic u'amea u'amea e tu'ufa'atasia tulaga lelei maualuga vevela ma lelei ductility ma weldability. E masani ona faʻaaogaina mo faʻaoga maualuga o le vevela ona o lona maualuga o le chromium ma le nickel e maua ai le malosi o le pala, lelei le tetee atu i le faʻamaʻiina, ma le malosi maualuga i le vevela e oʻo atu i le 2100 ° F. Ona o le maualuga o le chromium ma le nickel content, e sili atu nai lo le 304 poʻo le 309 stainless i le tele o siosiomaga.

Meatotino tau vailaau:

%	Cr	Ni	C	Si	Mn	P	S	Mo	Cu	Fe
310	min: 24.0 maualuga:26.0	min: 19.0 maualuga: 22.0	0.25	0.75	2.0	0.045	0.030	0.75	0.5	paleni
310S	min: 24.0 maualuga: 26.0	min: 19.0 maualuga: 22.0	0.08	1.00	2.0	0.045	0.030	0.75	0.5	paleni

Meatotino Fa'ainisinia:

Vasega	Malosi Tetele ksi (min.)	Malosi e maua mai 0.2% Offset ksi (min.)	Fa'aumiumi - % i 50 mm (min.)	Malosi (Brinell) MAX	Malosi (Rockwell B) MAX
310/310S	75	30	40	217	95

Meatotino Faaletino:

Denstiy lbm/in3	Coefficient o Fa'ateleina le vevela (min/in)-°F			Tete'e eletise mW-i totonu		Amioga vevela BTU/hr-ft-°F		BTU vevela ma'oti/lbm -°F	Malosi fa'amaneta (fa'a'ele'ele)1	Module o le Elasticity (fa'aluina)2-psi
i le 68 °F	i le 68 – 212°F	i le 68 – 932°F	i le 68 – 1832°F	i le 68°F	i le 1200°F	i le 68 – 1832°F	i le 68 – 932°F	i le 32 – 212°F	i le 200H	i le vevesi (E)	i sele (G)
0.29	8.8	9.5	10.5	30.7	—	10.5	10.8	0.12	1.02	29 x 106	11.2 x 106