ASTM A335 P22 Seamless Alloy Steel Pipe

ASTM A335 P22 is the part of ASTM A335. ASTM A335 P22 alloy steel pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.The range of ASTM A335 P22 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

Outer Dimensions: 19.05mm – 114.3mm
Wall Thickness: 2.0mm – 14 mm
Length: max 16000mm
Steel grade: ASTM A335 P22 

Surface treatment:
Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.Mechanical properties for ASTM A335 P11
Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.Material & Manufacture

ASTM A335 P22 Chemical Composition

C, %	Mn, %	P, %	S, %	Si, %	Cr, %	Mo, %
0.015 max	0.30-0.61	0.025 max	0.025 max	0.50 max	1.90-2.60	0.87-1.13

ASTM A335 P22 Properties

Tensile Strength, MPa	Yield Strength, MPa	Elongation, %
415 min	205 min	30 min

ASTM A335 Gr P22 Equivalent Material

ASTM	ASME	Equivalent material	JIS G 3458	UNS	BS	DIN	ISO	ABS	NK	LRS
A335 P22	SA335 P22	T22, 10CrMo910, 10CrMo9-10, 1.7380, 11CrMo9-10, 1.7383	STPA 24	K21590	3604 P1 622	17175 10CrMo910	2604 II TS34	ABS 13	KSTPA 24	Sec 2 2-1/4Cr1Mo410

 

Mechanical Tests Specified:

Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.

Notes for Bend Test:

For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

Related informations:
European Standards for steel
ASTM Standards for steel pipes
JIS Seamless Pipe
Tubes for Mechanical and Automobile
ASTM A335 Pipe Specifications
ASTM A333 Pipe Specifications
ASTM A213M-09 Standard Specication
How to packing the seamless pipe
Tubes in small calibers for boilers and petro chemical industry