2. SAE 8620 Steel Whakatakotoranga me nga Paerewa Tika
|
Whenua
|
USA |
DIN |
BS |
BS |
Hapani
|
|
Paerewa
|
ASTM A29 |
DIN 1654 |
EN 10084 |
BS 970
|
JIS G4103
|
|
Koeke
|
8620 |
1.6523/
21NiCrMo2
|
1.6523/
20NiCrMo2-2
|
805M20 |
SNCM220
|
3. ASTM 8620 Steels & Equivalents Chemical Composition
| Paerewa |
Kōeke |
C |
Mn |
P |
S |
Si |
Ni |
Cr |
Mo |
| ASTM A29 |
8620 |
0.18-0.23 |
0.7-0.9 |
0.035 |
0.040 |
0.15-0.35 |
0.4-0.7 |
0.4-0.6 |
0.15-0.25 |
| DIN 1654 |
1.6523/
21NiCrMo2 |
0.17-0.23 |
0.65-0.95 |
0.035 |
0.035 |
≦0.40 |
0.4-0.7 |
0.4-0.7 |
0.15-0.25 |
| EN 10084 |
1.6523/
20NiCrMo2-2 |
0.17-0.23 |
0.65-0.95 |
0.025 |
0.035 |
≦0.40 |
0.4-0.7 |
0.35-0.70 |
0.15-0.25 |
| JIS G4103 |
SNCM220 |
0.17-0.23 |
0.6-0.9 |
0.030 |
0.030 |
0.15-0.35 |
0.4-0.7 |
0.4-0.65 |
0.15-0.3 |
| BS 970 |
805M20 |
0.17-0.23 |
0.6-0.95 |
0.040 |
0.050 |
0.1-0.4 |
0.35-0.75 |
0.35-0.65 |
0.15-0.25 |
4. AISI 8620 Tikanga Miihini Miihini
Kiato (lb / cu. in.) 0.283
Te Kaha Motuhake 7.8
Wera Tauwhāiti (Btu/lb/Deg F – [32-212 Deg F]) 0.1
Ira Whakarewa (Deg F) 2600
Te Waariki 26
Te Whakawhanui Ngaaariki Coeff 6.6
Kōwae o te Elasticity Tension 31
- 8620 Nga Tikanga Hangarau maitai
| Āhuatanga |
Inenga |
Imperial |
| Te kaha tensile |
530 MPa |
76900 psi |
| Te kaha tuku |
385 MPa |
55800 psi |
| Kōwae rapa |
190-210 GPa |
27557-30458 ksi |
| Kōwae rahi (he angamaheni mo te maitai) |
140 GPa |
20300 ksi |
| Te kōwae kutikuti (te tikanga mo te maitai) |
80GPa |
11600 ksi |
| Te ōwehenga o Poisson |
0.27-0.30 |
0.27-0.30 |
| Izod Paanga |
115 J |
84.8 ft.lb |
| Te pakeke, Brinell |
149 |
149 |
| Te pakeke, Knoop (kua tahuri mai i te pakeke o Brinell) |
169 |
169 |
| Te pakeke, Rockwell B (kua tahuri mai i te pakeke o Brinell) |
80 |
80 |
| Te pakeke, Vickers (kua tahuri mai i te pakeke o Brinell) |
155 |
155 |
| Mahinga miihini (he wera te huri me te matao te kumea, i runga i te 100 machinability mo AISI 1212 maitai) |
65 |
65 |
5. Te hanga i nga mea 8620 Steel
Ko te rino koranu AISI 8620 ka hangai i te pāmahana timatanga o te 2250ºF (1230ºC) ki raro tata ki te 1700ºF(925ºC.) i mua i te whakamaroketanga o te wera me te waro. Ko te koranu ka whakamatao i te hau i muri i te hanga.
6. ASTM 8620 Tiaki Wera Tiaki
Ko te AISI 8620 te rino ka taea te whakakii i te katoa ma te wera ki te 820 ℃ - 850 ℃, ka pupuri kia rite te pāmahana puta noa i te waahanga me te whakamatao i roto i te oumu, i te hau makariri ranei.
Ko te whakamahana i nga waahanga wera me te wai tineia o nga tira 8620 (kaore i te waro) ka mahia i te 400 F ki te 1300 F hei whakapai ake i te pakari o te keehi me te iti o te paanga ki tona pakeke. Ma tenei ka whakaiti i te tupono o te huri kapiti.
Ko te AISI maitai 8620 ka austenitized a tawhio noa 840°C – 870°C, ka tineia te hinu, te wai ranei i runga i te rahi o te waahanga me te uaua. Matao ki te hau, ki te hinu ranei e hiahiatia ana.
1675ºF (910ºC) me te hau makariri. Ko tetahi atu tikanga mo te whakapai ake i te machinability i roto i 8620 rauemi; Ka whakamahia ano pea te whakamaarama i mua i te whakapakeketanga o te keehi.
7. Mahinga o SAE 8620 Steel
Ko te 8620 koranu rino ka ngawari ki te miihini i muri i te maimoatanga wera me te /ranei te carburizing, me iti rawa kia kore ai e pakaru te keehi pakeke o te waahanga. Ka taea te mahi miihini ma te tikanga tikanga i mua i te whakamahana wera – i muri i te mahi miihini waro ka iti noa ki te huri.
8. Welding of 8620 Materials
Ko te koranu 8620 ka paiherea hei ahua hurihuri ma nga tikanga tikanga, ko te nuinga o te hau, te pewa ranei. He pai te whakamahana i mua i te 400 F, me te whakamahana i muri i muri i te whakapiri ka tohutohuhia - tirohia te tikanga weld kua whakaaetia mo te tikanga i whakamahia. Heoi, karekau i te tūtohutia te whakapiri i roto i te keehi kua whakapakeketia, na roto ranei i te ahua pakeke
9. Te tono mo te ASTM 8620 Steel
Ko nga mea maitai AISI 8620 e whakamahia nuitia ana e nga waahanga ahumahi katoa mo nga waahanga marama ki te reo taumaha me nga rakau e hiahia ana kia kaha te whakakakahu o te mata me te kaha o te kaha matua me nga paanga.
Ko nga tono angamaheni ko: Arbors, Bearings, Bushings, Cam Shafts, Differential Pinions, Guide Pins, King Pins, Pistons Pins, Gears, Splined Shafts, Ratchets, Sleeves and other applications where it is good to have a steel that can be machined and carburized ki te hōhonutanga take mana.