Chemesch Zesummesetzung a mechanesch Eegeschaften:
ASTM A537 Class 3(A537CL3)
| MATERIAL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Class 3(A537CL3) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERIAL |
Tensile Strength (MPa) |
Yield Stäerkt (MPa) MIN |
% Verlängerung MIN |
| ASTM A537 Class 3(A537CL3) |
485-690 |
275-380 |
20 |
ASTM A537 Class 2(A537CL2)
| MATERIAL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Class 2(A537CL2) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERIAL |
Tensile Strength (MPa) |
Yield Stäerkt (MPa) MIN |
% Verlängerung MIN |
| ASTM A537 Class 2(A537CL2) |
485-690 |
315-415 |
20 |
ASTM A537 Class 1(A537CL1)
| MATERIAL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Class 1(A537CL1) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERIAL |
Tensile Strength (MPa) |
Yield Stäerkt (MPa) MIN |
% Verlängerung MIN |
| ASTM A537 Class 1(A537CL1) |
450-585 |
310 |
18 |
Referenzéierten Dokumenter
ASTM Standards:
A20/A20M: Spezifizéierung fir allgemeng Ufuerderunge fir Drockbehälterplacke
A435/A435: Fir Straight-Beam Ultrasonic Untersuchung vu Stahlplack
A577/A577M: Fir Ultraschall Wénkel-Beam Ënnersichung vun Stol Placke
A578/A578M: Fir Straight-Beam Ultrasonic Untersuchung vu Rolled Steel Placke fir speziell Uwendungen
Fabrikatioun Notizen:
Stahlplack ënner ASTM A537 Klass 1, 2 an 3 soll Stol ëmbruecht ginn a mat der fein austenitescher Kärgréisst Ufuerderung vun der Spezifizéierung A20/A20M entspriechen.
Wärmebehandlungsmethoden:
All Placke ënner ASTM A537 solle wéi follegt waarm behandelt ginn:
ASTM A537 Klass 1 Placke sollen normaliséiert ginn.
Klass 2 an Klass 3 Placke sollen ofgeschwächt an temperéiert ginn. D'Temperaturtemperatur fir Klass 2 Placke soll net manner wéi 1100 ° F [595 ° C] an net manner wéi 1150 ° F [620 ° C] fir Klass 3 Placke sinn.
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)