Cr12MoV calido involutus ferro per vectibus informationes
Ferrum Cr12MoV altam duritiem habet, et eae cum sectione transversali 300 ad 400 mm vel minus penitus extingui possunt.
Potest bonam duritiem sustinere et resistentiam in 300 400℃ sustinere, eius durities quam ferro Cr12 altior est, eiusque volubilis mutatio minima in exstinguendo est. Adhiberi potest varias formas et instrumenta fabricare cum magnis sectionibus, incompositis figuris, magnisque oneribus ictum sustinere. Exempli gratia, pulsare moritur complexis figuris, insertis complexu moritur, ferrum altum trahens perit, filum trahens perit, filum filo lina, frigus extrusio moritur, frigus secans forfices, serras circulares, instrumenta vexillum, instrumenta metientes, etc.
Cr12MoV chalybs summus carbo est, summus molybdenus lysic chalybs. Contentum carbonis eius multo minus est quam ferrum Crl2, et additur cum molybdeno et vanadio elementis, quae insigniter melioris proprietatum processus ferri scelerisque, ictum duritiem et distributionem carbidam. Ferrum magnum gerunt resistentiam, duritiem, duritiem, duritiem, stabilitatem scelerisque, vim compressivam, necnon deformationem microform, optimam comprehensivam perficiendi et amplam aptabilitatem. Calor molliens temperatus est 520℃. Magnitudo abscise infra 4mm est et penitus indurari potest. Vestis resistentiae huius chalybis est 3~4 partibus altior quam ferrum roboris humili, et volumen restinguendum parvum est. Altitudo obduratio: oleum exstinguentis 200~300mm.
In processu crystallizationis, magnae carbides eutecticae albae formantur (substantiae carbonised fractio circiter 20% est, et temperatura eutectica circiter 1150°C). Carbides hae sunt durissimae et fragiles. Etsi carbides ad aliquem gradum post rotam volvendam confractae sunt, carbides in vincula, tabulas, caudices et globulos secundum directionem volubilem distribuuntur, et gradus segregationis cum diametro ferri augetur.
Chemical et Mechanica
Chemical composition% of Cr12MoV chalybe
| C(％) |
Si(％) |
Mn(％) |
P(％) |
S(％) |
Cr(％) |
Ni(％) |
Mo(％) |
V(%) |
Cu(%) |
| 1.45～1.70 |
≤0.40 |
≤0.40 |
≤0.030 |
≤0.030 |
11.00～12.50 |
≤0.20 |
0.40～0.60 |
0.15～0.30 |
≤0.30 |
Mechanica gradus Cr12MoV
Probatur viribus
Rp0.2(MPa) |
Distrahentes fortitudo
Rm(MPa) |
Impact navitas
KV(J) |
Prolongatio ad fracturam
A(%) |
Reductio in sectione transversali fractura
Z(%) |
Ut-calor affectos Condition |
Brinell duritia (HBW) |
| 485(≥) |
154(≥) |
43 |
42 |
44 |
Solutio et Aging, Annealing, Ausaging, Q+T, etc |
112 |
Cr12MoV adumbrari ferrum admiscere
| Steel |
Praefixum terrestriale |
C(%) |
V(%) |
Si(%) |
Mn(%) |
P(%) |
S(%) |
Cr(%) |
| SKD11 |
CNS |
1.4-1.6 |
0.2-0.5 |
≦0.4 |
≦0.6 |
≦0.03 |
≦0.03 |
11.0-13.0 |
| Cr12MoV |
GB |
1.45-1.70 |
0.15-0.30 |
≦0.4 |
≦0.4 |
≦0.03 |
≦0.03 |
11.0-12.5 |
| SKD11 |
JIS |
1.4-1.6 |
0.2-0.5 |
≦0.4 |
≦0.6 |
≦0.03 |
≦0.03 |
11.0-13.0 |
| X165Cr-MoV12 |
DIN |
1.55-1.75 |
0.1-0.5 |
0.25-0.40 |
0.2-0.4 |
≦0.03 |
≦0.03 |
11.0-12.0 |
Cr12MoV ferro dolor productorum
| Genus productum |
Products |
Dimension |
Processes |
Libera Status |
| Plates/Sheets |
Plates/Sheets |
0.08-200mm(T)*W*L |
Fictor, calidus volubilis, frigidus volubilis |
Annealed, Solutio et senescentis, Q+T, ACID-ALUTATUS, iaculatus |
| Steel Bar |
Bar circum, Flat Bar, Quadratus Bar |
Φ8-1200mm*L |
Fictor, calidus volubilis et frigidus volvens, cast |
Atra, Aspera Conversio, Iaculatio. |
| Coil/Strip |
Steel Coil/ Steel Strip |
0.03-16.0x1200mm |
Frigidus-rolled & Hot-Rolled |
Annealed, Solutio et senescentis, Q+T, ACID-ALUTATUS, iaculatus |
| Fistula/Tubes |
Seamless Pipes / Tubes, iuncta Pipes / Tubes |
OD:6-219mm x WT:0.5-20.0mm |
Calidum extrusionem, frigus tractum, Welded |
Annealed, Solutio et Aging, Q+T, ACID-ALVIT |
Curatio caloris Cr12MoV Admisce Steel
spheroidizing furnum: 860℃ X 2h fornacem refrigerare ad 750℃, ac deinde fornacem refrigerare ad 500-550℃, removere et refrigerationem aeris
Restinctus + temperatus:1100℃ X 20min gradus exstinguiendi + 700℃ X 1h temperandi, removendi et aeris refrigerationem.
Exstinguere: 1030℃ X 40min oleum exstinguere (800℃ preheating, vacuum 2.5 ba) Temperatio: 250℃ X 1h.
Applicationem
Frigidum opus ferro perit, durities chalybs, restingueret, duritia temperans, resistentia induunt, robur Cr12 alcior est. Adhibetur in fabricando variarum frigorum biturarum peritorum et instrumentorum cum magnis transversis sectionibus, multiplicibus figuris et conditionibus gravium operationum, ut pulsare mori, tondet mori, limbis perit, profunda extractio perit, serra circularis, instrumenta vexillum, et medetur sequela volvens mori. , etc.