Chemical et Mechanica
Compositio chemica (wt.%) de gradu Cr12: GB/T 1229-2000
| Elementa |
Min.（≥） |
Max.（≤） |
| C |
2.00 |
2.30 |
| Si |
- |
0.40 |
| Mn |
- |
0.40 |
| Cr |
11.50 |
13.00 |
Mechanica rerum gradus Cr12 GB/T 1229-2000
Probatur viribus
Rp0.2 (MPa) |
Distrahentes fortitudo
Rm (MPa) |
Impact navitas
KV (J) |
Prolongatio ad fracturam
A (%) |
Reductio in sectione transversali de fractura
Z (%) |
Ut-calor affectos Condition |
Brinell duritia (HBW) |
| 539 (≥) |
215 (≥) |
42 |
14 |
42 |
Solutio et Aging, Annealing, Ausaging, Q+T, etc |
244 |
GB Cr12 mixtura instrumentum ferreum materiale aequipollens -UNS T30403
| Gradus |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
V |
| D3 |
2.00～2.35 |
0.10～0.60 |
0.20～0.60 |
0.003 MAX |
0.003 MAX |
11.0～13.5 |
~ |
1.00 MAX |
| SKD1 |
1.90～2.20 |
0.10～0.60 |
0.20～0.60 |
0.003 MAX |
0.003 MAX |
11.0～13.0 |
~ |
0.30 MAX |
| Cr12 |
2.00～2.30 |
0.40 MAX |
0.40 MAX |
0.003 MAX |
0.003 MAX |
11.50～13.00 |
~ |
~ |
| 1.2080/ X210Cr12 |
1.90～2.20 |
0.10～0.40 |
0.15～0.45 |
0.003 MAX |
0.003 MAX |
11.00～12.00 |
~ |
~ |
Applicationes Cr12 materia ferro
Cr12 chalybs est proprium offensionis instrumentum chalybeum, Cr12 est Seres frigus Opus Admisce Morsus Steel. Frigidum opus Mechanica Properties valde nice. Cr12 chalybe magna abrasione resistentia, deformatio microform laboris frigidi mori ferro, ventus instrumentum ferreum ferreum, contentum carbonis usque ad 1.5%, chromium contentum usque ad 11.5%, calor curatio duritiem attingere potest 60 HRC. Cr12 sectione ferro adhiberi potest ad：
a) Pii mori maxime adhibetur pro parvis dynamicis condicionibus loaGBg magno labore resistendi requirentibus, simplex figura trahens et blank moritur.
b Ratio fabricandi benGBg fingit in altum indutum, complexa figura ferrum, mori, interiicere, facere ferrum, quando alea suadetur, duritia 60~64HCR.
c) ad conficiendum moriendum induendi fabricandum requiritur, commendatur duritiem 62~64HCR.
d) aluminium anti- frigidum, extrusionem mori ferrum, commendatur duritiem 60~62HCR.
e) pro benGBg carbonis contentum 0.65% ad 0.80% probationem ferro builGBg, duritiem 60~ 62HCR.
f) Ad tabescentium moriendum adhiberi potest, ferrum, rotas volvens, laminas tondendas, fri- heaGBg mori, lutum fingunt.
g) Ad thermoset molGBg formas plasticas adhiberi potest.
Cr12 ex ferro materia cudebat
Preheat lente ad 900~950°C deinde caliditatem celerius ad 1050-1100 °C augendam. Noli cudere infra 1020°C. Deinde tardius post cudendum Cr12 refrigerant.
Annealing of Cr12 chalybe material
GB Cr12 instrumentum chalybeum condi- tionis normale in furnum et machinabile traditur. Si opus re- furnum. Calefacit Cr12 chalybem CM °C et macera penitus, tunc refrigerabis in fornace. Post furnum, in Cr12 partus duritia est 255HB Max.
Accentus Sublevatio Cr12 ferro material
Quando debent instrumenta ex ferro mixtura facta ex ferro graviter machinata vel trita sunt, subsidia modorum internorum expedit ante obdurationem ad extenuandum possibilitatem corruptelam. Accentus sublevatio est valde necessaria, accentus sublevatio fieri debet post machinam asperam. Ut levare vis, elementum diligenter ad 600-650°C calefaciat, tempus bene bibulae permittit (duobus horis per 25mm sectionis imperandi). Frigus in fornace vel aere. Instrumenta ante obdurationem machined finiendum.
Obduratio materiae Cr12 ferro
GB Cr12 Partus condicio plerumque est Annealing, itaque durities necessaria est. Instrumenta Cr12 calefaciunt in fornace temperata, si fornacem non continentem habent, duritia pravorum valde commendatur. Pre-calor Cr12 instrumentum ferri ad 750~800°C, tempus satis maceret donec calor perveniat. Inde usque ad 1000-1040 °C adduci, restinguendo aere vel oleo refrigerando.
Temperatio materiae Cr12 ferro
Cale GB Cr12, Calor temperaturae debitae uniformiter praebens bibula tempus duarum horarum per 25mm sectionis imperandi. Recede a fornace et refrigerandi aeris. Diversa temperantia temperamentum diversum duritiem habebit. Temperatio typica 204°C est, post duritiam temperandam 61HRc Min.
Cr12 materia ferro welding
In genere, non monemus welGBg ferri instrumenti mixturae, sed utentes interdum pactionem malunt ad evitandas dispendii sumptus. Sciendum est hunc gradum aeris duritia esse chalybem et in welGBg area glutino temperaturam circiter 1000°C attingere. Solet autem fieri in refrigerio, nisi caute adhibeantur. Popularis modi welGBg sunt hydrogenii atomi et arcus argonis. Commendamus tibi cum elit welGBg consumables contactum qui tibi plenum auxilium praebere debet ac informationes in ferro welGBg mixturae ferri.
Nitriding de materia ferro Cr12
Cr12 stannum instrumentum ferreum nitri potest ad casum superficiei duram reddendam. Post curationem caloris nitriGBg, in Cr12 tunc valde repugnans ad induendum et exesa est. NitriGBg etiam resistentia auget ad corrosionem.
Final molendum de materia Cr12 ferro
GrinGBg GB Cr12 Ferro. Rectum rotae gradum in consultatione cum fabrica grinGBg rotae elige. Curat grinGBg rotam in bono statu per instrumentum congruum. Uda grinGBg potior est optio copiosis refrigerandi utendi. Si siccum grinGBg confertur, tum rota mollissima utatur.