Technicae conditiones
S890Q/S890QL/S890QL1 Chemical composition %
| Materia |
Qualitas |
C |
Mn |
Si |
P |
S |
| S890Q/S890QL/S890QL1 HSLA lamina ferrea |
/ |
≤0.20 |
≤1.70 |
≤0.80 |
≤0.025 |
≤0.015 |
| L |
≤0.020 |
≤0.010 |
| L1 |
≤0.020 |
≤0.010 |
S890Q/S890QL/S890QL1 Mechanica proprietates in tabulis
| Materia |
Vires fac σ0.2 MPa |
Vis tensibilis σ MPa |
Prolongatioδ5 % |
V Impact
Longitudines |
| ≥6- 50 |
＞50-100 |
≥6 -50 |
＞50-100 |
| S890Q |
≥890 |
≥870 |
900-1060 |
≥13 |
-20℃ ≥30J |
| S890QL |
-40℃ ≥30J |
| S890QL1 |
-60℃ ≥30J |
S890QL Ferro extincta et temperata structuralis
Hot-formando
Calidum supra 580°C fieri potest. Exstinctio et temperantia sequens secundum condiciones traditionis exercenda est.
Milling
HSSCO EXERCITATIO cobalta ferro commixto cursu. Celeritas secans debet esse circiter 17 - 19 m/ min. Si HSS terebras adhibentur, celeritas secans esse debet circiter 3 – 5 m/ min.
Flammae Secans
Temperatio materiae saltem RT ad sectionem flammeam esse debet. Praeterea hae temperaturae preheating commendantur quibusdam crassitudinibus lamellarum: Nam laminae crassitudines super 40mm, preheat ad 100°C et ad crassitudines super 80mm, preheat ad 150°C.
Welding
S890QL Ferrum omnibus modis glutino aptum est. Temperatio materiae saltem RT ad glutino esse debet. Praeterea sequentia temperaturae preheating commendantur quibusdam crassitudinibus lamellarum;
20mm – 40mm: 75°C
Plus 40mm: 100°C
60mm et supra: CL°C
Haec indicia sunt valores normae tantum, in principio, indicia SEW 088 observanda sunt.
Tempus t 8/5 debet esse inter 5 et 25 s, secundum artem glutino adhibitam. Si levamen furnum accentus ad rationes constructiones necessarias sit, id fieri debet in amplitudine temperatura 530°C-580°C .