410HT ferro intemerata

Admisceri 410 HT propositum est basicum, generale, calor versionis Typi tractata 410. Genus martensiticum est, ad propositum generale adhibitum, ubi corrosio non est gravis. Admisce 410 minimum continet chromium 11.5% quod tantum sufficit ad corrosionem resistentiae demonstrandam proprietates atmosphaerae lenis, vaporis et multae culturae chemicae lenis.

Chemical Properties:

	C	Mn	Si	P	S	Cr	Ni
410HT	0.15 max	1.00 max	1.00 max	0.04 max	0.03 max	min: 11.5 max: 13.5	0.50 max

Mechanica Properties:

Gradus	Distrahens fortitudo ksi (MPa) min	0,2% offset ksi (MPa) min	Prolongatio (% in 50mm) min	Duritia (Brinell) MAX*	Duritia (Rockwell B) MAX
410HT	65 (450)	30 (205)	20

Signa:

• ASTM/ASME: UNS S41000
• EURONORM: FeMi35Cr20Cu4Mo2
• DIN: 2.4660

Corrosio resistendi:

• Bonum corrosio resistendi ad corrosionem atmosphaericum, aquam potabilem, et ad ambitus leniter mordax
• Expositio eius ad cotidianas actiones (ludis, praeparatio cibi) plerumque satisfacit, cum purgatio propria fit expositi usus
• Bonum corrosionis resistentia ad concentrationes humiliandas acida organica et mineralia

Characteres welding

• Facile iuncta omnibus modis vexillum
• Ad periculum creptionis reducendum, suggeritur praecalescere operis particulam ad 350 ad 400oF (177 ad 204oC)
• Post pugillum furnum commendatur ad maximum ductilis conservandum

Calor treatment

• Proprium opus calidum range est 2000 ad 2200oF (1093 ad 1204oC)
• Non operantur hanc materiam infra 1650oF (899oC)

Mechanica Proprietates Caloris agitur 410;

Calor treatment	T410 (0.14%C) Hardened 1800°F (982°C)
	Rockwell duritia	0.2% YS, Ksi (MPa)	UTS, Ksi (MPa)
Annealed*	81 HRB	45.4  (313)	80.4  (554)
Hardened & Tempered 400°F (204°C)	43 HRC	156.1   (1076)	202.9   (1399)
Harded & Tempered 550°F (288°C)	40 HRC	148.3  (1022)	187.0   (1289)
Harded & Tempered 600°F (316°C)	40 HRC	148.8   (1026).	186.1   (1283)
Hardened & Tempered 800°F (427°C)	41 HRC	132.9 (916)	188.5   (1300)
Hardened & Tempered 900°F (482°C)	41 HRC	122.6 (845)	154.3   (1063)
Induratus & temperatus 1000°F (538°C)	35 HRC	127.9  (882)	154.3   (1063)
Hardened & Tempered 1200°F (649°C)	98 HRB	85.5   (589)	111.2  (767)

Applicationes:

Applicationes ad resistentiam corrosionis modicam requirunt et proprietates mechanicae altae sunt ideales ad Alloy 410HT. Exempla applicationum quae frequentius admisceantur 410HT includunt:

• Cutlery
• Vapor et Gas Turbine laminae
• Culina utensilia
• Repagula, nuces, ANISOCYCLUM
• Sentinam et valvae partes et spicula
• Meum scalae tegetis
• Instrumenta dentalia et chirurgica
• Nozzles
• Globos ferro indurato sedilia oleum bene soleatus