CCS plakaya pola avakirina keştiyê

CCS Shipbuilding Plate

CCS Grade FQ70 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.18	0.55	1.60	0.020	0.020	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
690	770-940	14

CCS Grade EQ70 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.20	0.55	1.70	0.025	0.025	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
690	770-940	14

CCS Grade DQ70 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.21	0.55	1.70	0.035	0.035	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
690	770-940	14--16

CCS Grade AQ70 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.21	0.55	1.70	0.030	0.030	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
690	770-940	14

CCS Grade EQ63 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.20	0.55	1.70	0.025	0.025	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
620	720-890	15

CCS Grade FQ63 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.18	0.55	1.60	0.020	0.020	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
620	720-890	15

CCS Grade AQ63 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.21	0.55	1.70	0.030	0.030	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
620	720-890	15

CCS Grade EQ56 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.20	0.55	1.70	0.025	0.025	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
550	670-830	16

CCS Grade FQ56 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.18	0.55	1.60	0.020	0.020	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
550	670-830	16

CCS Grade AQ56 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.21	0.55	1.60	0.030	0.030	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
550	670-830	16

CCS Grade EQ51 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.20	0.55	1.70	0.025	0.025	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
500	610-770	16

CCS Grade FQ51 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.18	0.55	1.60	0.020	0.020	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
500	610-770	16

CCS Grade AQ51 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.21	0.55	1.70	0.030	0.030	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
500	610-770	16

CCS Grade EQ47 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.20	0.55	1.70	0.025	0.025	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
460	570-720	17

CCS Grade FQ47 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.18	0.55	1.60	0.020	0.020	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
460	570-720	17

CCS Grade AQ47 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	N max.
0.21	0.55	1.70	0.030	0.030	0.020

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
460	570-720	17

CCS Grade EH40 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	Als	Nb	V	Ti max.	Cu max.	Cr max.	Ni max.	Mo max.	N max.
0.18	0.50	0.90-1.60	0.025	0.025	0.015	0.02-0.05	0.05-0.10	0.02	0.35	0.20	0.40	0.08	-

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
390	510-660	20

CCS Grade FH40 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	Als	Nb	V	Ti max.	Cu max.	Cr max.	Ni max.	Mo max.	N max.
0.16	0.50	0.90-1.60	0.020	0.020	0.015	0.02-0.05	0.05-0.10	0.02	0.35	0.20	0.80	0.08	0.009

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
390	510-660	20

CCS Grade AH40 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	Als	Nb	V	Ti max.	Cu max.	Cr max.	Ni max.	Mo max.	N max.
0.18	0.50	0.90-1.60	0.030	0.030	0.015	0.02-0.05	0.05-0.10	0.02	0.35	0.20	0.40	0.08	-

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
390	510-660	20

CCS Grade EH36 Shipbuilding Plate Steel

C max	Si max	Mn	P max	S max	Als	Nb	V	Ti max.	Cu max.	Cr max.	Ni max.	Mo max.	N max.
0.18	0.50	0.90-1.60	0.025	0.025	0.015	0.02-0.05	0.05-0.10	0.02	0.35	0.20	0.40	0.08	-

Hêza Hilberînê (MPa) min.	Hêza Tensilê (MPa)	Dirêjbûn min. %
355	490-630	21

CCS/E Hêza Asayî ya Max Pêkhatina Kîmyewî ya li Germiya Germiyan

Pêve	CCS E Max %	Pêve	CCS E Max %
C	0.21	Ni
Mn	0.60	Mo
Si	0.1-0.35	Al
S	0.035	Nb
P	0.035	V
Cu		Ti
Cr		N

Hestiyariya qirikê: Pcm = (C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+ 5B)%
Wekheviya karbonê: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
CCS/E Taybetmendiya hêza asayî ya di Germiya rijandin de

Sinif	Qewîtî	Hêza Hilberînê	Tensile Strength	Dirêjbûn	Enerjiya Bandora
(mm)	MPa (min)	MPa	% (min)	(KV J) (min)
				-20 derece
CCS E	8-240	235	400-520	22	27J

Nîşe: enerjiya bandorê di binê stûrahiya kêmtir 50 mm; enerjiya bandora min ya dirêj

CCS/D Hêweya normal ya herî zêde pêkhatina kîmyewî ya di germ-hildanê de

Pêve	CCS D  Max %	Pêve	CCS D  Max %
C	0.21	Ni
Mn	0.60	Mo
Si	0.1-0.35	Al
S	0.035	Nb
P	0.035	V
Cu		Ti
Cr		N

Hestiyariya şikestê:  Pcm = (C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+ 5B)%
Wekheviya karbonê:  Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

CCS/D  Taybetmendiya hêza asayî ya di Hot-rolled de

Sinif	Qewîtî	Hêza Hilberînê	Tensile Strength	Dirêjbûn	Enerjiya Bandora
(mm)	MPa (min)	MPa	% (min)	(KV J) (min)
				-20 derece
CCS D	8-240	235	400-520	22	27J

Nîşe: enerjiya bandorê di binê stûrahiya kêmtir 50 mm; enerjiya bandora min ya dirêj

CCS/B Hêza normal ya pêkhatina kîmyewî ya herî zêde ya di germ-hildanê de

Pêve	CCS B  Max %	Pêve	CCS B  Max %
C	0.21	Ni
Mn	0.80	Mo
Si	0.35	Al
S	0.035	Nb
P	0.035	V
Cu		Ti
Cr		N

Hestiyariya şikestê:  Pcm = (C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+ 5B)%
Wekheviya karbonê:  Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

CCS/B  Taybetmendiya hêza asayî ya di Germûla de

Sinif	Qewîtî	Hêza Hilberînê	Tensile Strength	Dirêjbûn	Enerjiya Bandora
(mm)	MPa (min)	MPa	% (min)	(KV J) (min)
				0 derece
CCS B	8-240	235	400-520	22	27J

Nîşe: enerjiya bandorê di binê stûrahiya kêmtir 50 mm; enerjiya bandora min ya dirêj

CCS/A Pêksaziya Kîmyewî ya Hêza Asayî ya herî zêde ya di Germê de

Pêve	CCS A Max %	Pêve	CCS A Max %
C	0.21	Ni
Mn	2,5*C MIN	Mo
Si	0.50	Al
S	0.035	Nb
P	0.035	V
Cu		Ti
Cr		N

​
Hestiyariya şikestê:  Pcm = (C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+ 5B)%
Wekheviya karbonê:  Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

CCS/A Taybetmendiya hêza asayî ya di Hot-rolled de

Sinif	Qewîtî	Hêza Hilberînê	Tensile Strength	Dirêjbûn	Enerjiya Bandora
(mm)	MPa (min)	MPa	% (min)	(KV J) (min)
				20 derece
CCS A	8-240	235	400-520	22

Nîşe: enerjiya bandorê di binê stûrahiya kêmtir 50 mm; enerjiya bandora min ya dirêj