S890Q/S890QL/S890QL1 Komposisi kimia %
| Bahan |
Kualitas |
C |
Mn |
Si |
P |
S |
| S890Q/S890QL/S890QL1 HSLA pelat baja |
/ |
≤0.20 |
≤1.70 |
≤0,80 |
≤0,025 |
≤0,015 |
| L |
≤0,020 |
≤0,010 |
| L1 |
≤0,020 |
≤0,010 |
S890Q/S890QL/S890QL1 Sifat mekanik ing tabel
| Bahan |
Kekuwatan ngasilake σ0,2 MPa |
Kekuatan tarik σb MPa |
Elongasiδ5 % |
V Dampak
Lengthways |
| ≥6- 50 |
＞50-100 |
≥6 -50 |
＞50-100 |
| S890Q |
≥890 |
≥870 |
900-1060 |
≥13 |
-20 ℃ ≥30J |
| S890QL |
-40 ℃ ≥30J |
| S890QL1 |
-60 ℃ ≥30J |
S890QL Quenched lan Tempered Struktural Steel
Panas-Forming
Bisa dadi panas ing ndhuwur 580 ° C. A quenching lan tempering sakteruse kudu ditindakake miturut kondisi pangiriman.
Penggilingan
Pengeboran nganggo baja kacepetan dhuwur campuran kobalt HSSCO. Kacepetan nglereni kudu kira-kira 17 - 19 m/min. Yen latihan HSS digunakake, kacepetan nglereni kudu kira-kira 3 - 5 m /min.
Flame-Motong
Suhu materi kudu paling sethithik RT kanggo nglereni geni. Kajaba iku, suhu preheating ing ngisor iki dianjurake kanggo kekandelan piring tartamtu: Kanggo kekandelan piring luwih saka 40mm, preheat nganti 100°C lan kanggo ketebalan luwih saka 80mm, preheat nganti 150°C.
Welding
S890QL baja cocok kanggo kabeh cara welding saiki. Suhu materi kudu paling sethithik RT kanggo welding. Kajaba iku, suhu preheating ing ngisor iki dianjurake kanggo kekandelan piring tartamtu:
20mm – 40mm: 75°C
Luwih saka 40mm: 100°C
60mm lan luwih: 150°C
Indikasi kasebut mung minangka nilai standar, ing prinsip, indikasi SEW 088 kudu dipatuhi.
Ing t 8 / 5 kaping kudu antarane 5 lan 25 s, gumantung ing technique welding digunakake. Yen anil relief stres perlu kanggo alasan konstruksi, iki kudu ditindakake ing kisaran suhu 530°C-580°C.