Komposisi Kimia lan Sifat Mekanik:
ASTM A537 Kelas 3 (A537CL3)
| MATERI |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Kelas 3 (A537CL3) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERI |
Kekuwatan Tarik (MPa) |
Kekuwatan Ngasilake (MPa) MIN |
% Elongasi MIN |
| ASTM A537 Kelas 3 (A537CL3) |
485-690 |
275-380 |
20 |
ASTM A537 Kelas 2 (A537CL2)
| MATERI |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Kelas 2 (A537CL2) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERI |
Kekuwatan Tarik (MPa) |
Kekuwatan Ngasilake (MPa) MIN |
% Elongasi MIN |
| ASTM A537 Kelas 2 (A537CL2) |
485-690 |
315-415 |
20 |
ASTM A537 Kelas 1 (A537CL1)
| MATERI |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Kelas 1 (A537CL1) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERI |
Kekuwatan Tarik (MPa) |
Kekuwatan Ngasilake (MPa) MIN |
% Elongasi MIN |
| ASTM A537 Kelas 1 (A537CL1) |
450-585 |
310 |
18 |
Dokumen Referensi
Standar ASTM:
A20/A20M: Spesifikasi kanggo Keperluan Umum kanggo Plate Kapal Tekanan
A435/A435: Kanggo Pemeriksaan Ultrasonik Lurus-Beam Plat Baja
A577/A577M: Kanggo Ultrasonik Sudut-Beam Pemeriksaan Plat Baja
A578/A578M: Kanggo Pemeriksaan Ultrasonik Lurus-Beam Plat Baja Gulung kanggo Aplikasi Khusus
Cathetan Manufaktur:
Piring baja miturut ASTM A537 Kelas 1, 2 lan 3 kudu dipateni baja lan tundhuk karo syarat ukuran gandum austenitik sing apik saka Spesifikasi A20/A20M.
Metode Perawatan Panas:
Kabeh piring miturut ASTM A537 kudu diolah kaya ing ngisor iki:
Piring ASTM A537 Kelas 1 kudu dinormalisasi.
Piring kelas 2 lan kelas 3 kudu dipateni lan digawe panas. Suhu tempering kanggo piring Kelas 2 ora kudu kurang saka 1100°F [595°C] lan ora kurang saka 1150°F [620°C] kanggo piring Kelas 3.