S890Q/S890QL/S890QL1 Chemical mejupụtara %
| Ihe onwunwe |
Ogo |
C |
Mn |
Si |
P |
S |
| S890Q / S890QL/ S890QL1 HSLA ígwè efere. |
/ |
≤0.20 |
≤1.70 |
≤0.80 |
≤0.025 |
≤0.015 |
| L |
≤0.020 |
≤0.010 |
| L1 |
≤0.020 |
≤0.010 |
S890Q/ S890QL/ S890QL1 Mechanical Njirimara na tebụl
| Ihe onwunwe |
Ike mpụta σ0.2 MPa |
Ike ike σb MPa |
Mgbatị 5 % |
V Mmetụta
Ogologo ogologo |
| ≥6-50 |
＞50-100 |
≥6-50 |
＞50-100 |
| S890Q |
≥890 |
≥870 |
900-1060 |
≥13 |
-20℃ ≥30J |
| S890QL |
-40℃ ≥30J |
| S890QL1 |
-60℃ ≥30J |
Steel Structural S890QL kwụsịrị na iwe ọkụ
Na-ekpo ọkụ-akpụkọ
Ịkpụ ọkụ n'elu 580 ° C ga-ekwe omume. A ga-emenyụ ọkụ na iwe na-esote dịka ọnọdụ nnyefe siri dị.
Ịgba igwe
Ngwongwo igwe na-agba ọsọ nke cobalt-alloyed HSSCO. Ọsọ ịkpụ kwesịrị ịdị ihe dịka 17 - 19 m / min. Ọ bụrụ na ejiri HSS eme ihe, ịbelata ọsọ kwesịrị ịdị ihe dịka 3 - 5 m /min.
Ịcha ọkụ
Ọnọdụ okpomọkụ nke ihe kwesịrị ịbụ ma ọ dịkarịa ala RT maka igbutu ọkụ. Na mgbakwunye, a na-atụ aro ikpo ọkụ ọkụ ndị a maka ụfọdụ ọkpụrụkpụ efere: Maka okpomoku dị elu karịa 40mm, kpoo ọkụ ruo 100 Celsius C yana maka ọkpụrụkpụ karịa 80mm, kpoo ọkụ ruo 150 Celsius.
ịgbado ọkụ
S890QL ígwè bụ adabara niile ugbu a ịgbado ọkụ ụzọ. Ọnọdụ okpomọkụ nke ihe kwesịrị ịbụ ma ọ dịkarịa ala RT maka ịgbado ọkụ. Na mgbakwunye, a na-atụ aro ikpo ọkụ ọkụ ndị a maka ụfọdụ ọkpụrụkpụ efere:
20mm - 40mm: 75°C
Ihe karịrị 40mm: 100C
60mm na karịa: 150°C
Ihe ngosi ndị a bụ ụkpụrụ ọkọlọtọ naanị, n'ụkpụrụ, ihe ngosi nke SEW 088 kwesịrị ịrapagidesi ike.
Oge t 8/5 kwesịrị ịdị n'etiti 5 na 25 s, dabere na usoro ịgbado ọkụ ejiri. Ọ bụrụ na mgbakasị ahụ mgbakasị ahụ dị mkpa maka ihe eji arụ ọrụ, ekwesịrị ime nke a na oke okpomọkụ nke 530C-580C.