Ihe igwe anaghị agba nchara 17-4PH

17-4PH na-ekpo ọkụ ngwa ngwa. N'oge ọgwụgwọ okpomọkụ ma ọ bụ na-akpụ akpụ, ekwesịrị izere ikuku nchebe nwere carbon ma ọ bụ nitrogen. Enwere ike itinye ihe ndị a n'elu nchara ma nye akpụkpọ anụ austenitic dị nro. Ọ bụrụ na achọrọ ikuku nchebe, a na-atụ aro argon ma ọ bụ helium.

Alloy na-enwekwa ike siri ike mgbe a na-agba ya, ebe ọgwụgwọ okpomọkụ dị mkpụmkpụ na-ebelata ọgụ na ncha. Ọzọkwa, 17-4PH dị mfe igwe na imepụta.

N'ihi ihe ndị bara uru, 17-4PH na-ahụta ojiji na ụlọ ọrụ dị iche iche. Akụkụ ndị a na-ahụkarị gụnyere akara igwe, patch mmanụ, na ogwe mgbapụta.

Enwere ike ịmegharị machinability 17-4PH na ọnọdụ annealed ngwọta yana ọnọdụ mmiri ozuzo siri ike. N'ihi na okpomọkụ ọgwụgwọ okpomọkụ ikpeazụ dị ala, 17-4PH nwere ike ịmegharị ya na njedebe ikpeazụ na ọnọdụ annealed wee mee agadi na-enweghị mgbanwe dị ukwuu ma ọ bụ scaling ma ọ bụrụ na akụkụ ahụ buru ibu, mgbe a ga-enye ohere maka nkwụsị na ịka nká.
Na ọnọdụ annealed machining bụ naanị obere obere dị iche na 300 usoro austenitic igwe anaghị agba nchara. N'ọnọdụ H900 ọnụ ọgụgụ igwe eji arụ ọrụ bụ 60% nke ahụ maka ihe annealed.

NKWUKWU kemikal

Akara ule	SS316	17-4PH
Carbon	0.05	0.06
Manganese	2	0.9
Phosphorous	0.045	0.03
sọlfọ	0.03	0.02
Silikoni	N/A	0.9
Ọla kọpa, columbium, na Tantalum	N/A	4
Molybdenum	2.1	N/A
Nickel	8	4
Chromium	18	17.5

Njirimara hysical nke igwe anaghị agba nchara 17-4PH

Ngwongwo	Imperial	Metric
Oke agbaze	2560-2625 °F	1404-1440 Celsius
Okpomọkụ akọwapụtara	0.11 Btu/lb.-°F	460 Joules /gg-K
Njupụta dị iche iche	0.282 lb /in3	7.8g /cm3
Eletriki Resistivity	38.6 μΩ n'ime	98 µΩ cm
Ọnụọgụ Linear nke Mgbasa ọkụ (70 °F ruo 200 Celsius) (21 Celsius C ruo 93 Celsius)	6 [na/na/°F·106]	10.8 [μm/m·°C]
Ọnụọgụ Linear nke Mgbasa ọkụ (70 °F ruo 400 Celsius) (21 Celsius C ruo 204 Celsius)	6 [na/na/°F·106]	10.8 [μm/m·°C]
Ọnụọgụ Linear nke Mgbasa ọkụ (70 °F ruo 600 Celsius) (27 Celsius C ruo 316 Celsius)	6.2 [na /na/°F·106]	11.2 [μm/m·°C]
Ọnụọgụ Linear nke Mgbasa ọkụ (70 °F ruo 800 Celsius) (21 Celsius C ruo 427 Celsius)	6.3 [na/na/°F·106]	11.2 [μm/m·°C]
Mmetụta okpomọkụ (@ 300 °F) (@ 149 Celsius)	124 Btu / (hr/ft² / na/°F)	17.9 [W/m-K]
Mmetụta okpomọkụ (@ 500 °F) (@ 260 Celsius)	135 Btu / (hr/ft²/na/°F)	19.5 [W/m-K]
Mmetụta okpomọkụ (@ 860 °F) (@ 460 Celsius)	156 Btu / (hr/ft² / na/°F)	22.5 [W/m-K]
Mmetụta okpomọkụ (@ 900 °F) (@ 482 Celsius)	157 Btu / (hr/ft² / na/°F)	22.6 [W/m-K]
Oke Poisson (Ọnọdụ H900)	0.272	0.272
Modulus nke ngbanwe (Ọnọdụ H900)	28 x 106 ksi	197 x 103 MPa
Modul nke Rigidity na Torsion	9.68 x 103 ksi	67 x 103 MPa

Ngwa igwe anaghị agba nchara 17-4PH

Ngwongwo	Imperial	Metric
Ike tensile kacha	23,300 psi	160 MPa
Ike Mpụta (0.02%)	16,680 psi	115 MPa
Mgbatị (% na 2")	5%	5%
Rockwell Hardness C	35	35

Ọgwụgwọ okpomọkụ

Igwe anaghị agba nchara 17-4PH dị na ngwọta annealed ọnọdụ na 1900 °F (1038 °C) na mgbe ahụ ikuku jụrụ ka 90 °F (32 °C).

Otú ọ dị, ọgwụgwọ okpomọkụ ndị ọzọ nwere ike ịmepụta ọkwa siri ike na ike dị iche iche. Edepụtara ọgwụgwọ ndị a na-ahụkarị na tebụl n'okpuru.

Ọnọdụ	Okpomọkụ [± 15 °F (± 8.4 °C)]	Usoro jụrụ oyi na Ogologo oge
H 900	900 °F (482 Celsius)	Ikuku jụrụ oyi maka elekere 1
H 925	925 °F (496 Celsius)	Ikuku jụrụ maka awa 4
H 1025	1025 °F (551 Celsius)	Ikuku jụrụ maka awa 4
H 1075	1075 °F (580 Celsius)	Ikuku jụrụ maka awa 4
H 1100	1100 °F (593 Celsius)	Ikuku jụrụ maka awa 4
H 1150	1150 °F (621 Celsius)	Ikuku jụrụ maka awa 4
H 1150 + 1150	1150 °F (621 Celsius) ndị sotere 1150 °F (621 Celsius)	Ikuku jụrụ maka awa 4 ndị sotere Ikuku jụrụ maka awa 4
H 1150-M	1400 °F (760 Celsius) ndị sotere 1150 °F (621 Celsius)	Ikuku jụrụ maka awa 2 ndị sotere Ikuku jụrụ maka awa 4