410HT igwe anaghị agba nchara mpempe akwụkwọ

Alloy 410 HT bụ ihe bụ isi, ebumnuche zuru oke, ụdị  ekpo ọkụ na-agwọ ụdị 410. Ọ bụ ụdị martensitic, eji eme ya maka ebumnuche izugbe, ebe corrosion adịghị njọ. Alloy 410 nwere opekempe nke 11.5% chromium nke zuru oke iji gosipụta ihe mgbochi corrosion na ikuku dị nro, uzuoku, na ọtụtụ gburugburu kemịkalụ dị nro.

Njirimara kemịkalụ:

	C	Mn	Si	P	S	Cr	Ni
410HT	0.15 kacha	1.00 kacha	1.00 kacha	0.04 kacha	0.03 kacha	Nkeji: 11.5 Oke: 13.5	0.50 kacha

Ngwongwo igwe:

Ọkwa	Ike tensile ksi (MPa) min	Mpụta Ike 0.2% akwụ ụgwọ ksi (MPa) min	Mgbatị (% na 50mm) min	Isi ike (Brinell) MAX	Isi ike (Rockwell B) MAX
410HT	65 (450)	30 (205)	20

Ụkpụrụ:

• ASTM/ASME: UNS S41000
• EURONORM: FeMi35Cr20Cu4Mo2
• Ọnụ: 2.4660

Nguzogide corrosion:

• Ezigbo nguzogide corrosion na-eguzogide corrosion ikuku, mmiri a na-aṅụ mmanya, na gburugburu ebe ndị na-emebi emebi.
• Ikpughe ya na ihe omume kwa ụbọchị (egwuregwu, nkwadebe nri) na-enye afọ ojuju mgbe a na-eme nhicha nke ọma mgbe ekpughere ya.
• Ezigbo nguzogide corrosion na obere mkpokọta organic na mineral acid dị nro

Njirimara ịgbado ọkụ

• Ejiri usoro ọkọlọtọ niile gbadoro ngwa ngwa
• Iji belata ihe ize ndụ nke mgbawa, a na-atụ aro ka ị kpoo akụkụ ọrụ ahụ ruo 350 ruo 400oF (177 ruo 204oC)
• A na-atụ aro ikpochapụ weld weld ka ọ na-ejigide ductility kacha

Ọgwụgwọ okpomọkụ

• Ogologo ọrụ ọkụ kwesịrị ekwesị bụ 2000 ruo 2200oF (1093 ruo 1204oC)
• Arụla ihe a n'okpuru 1650oF (899oC)

Njirimara arụrụ arụ nke Okpomọkụ Agwọ 410:

Ọgwụgwọ okpomọkụ	T410 (0.14%C) agbasie ike 1800°F (982°C)
	Rockwell Hardness	0.2% YS, Ksi (MPa)	UTS, Ksi (MPa)
Ewepụrụ*	81 HRB	45.4 (313)	80.4 (554)
Agbasie Ike & Ọkụ 400°F (204°C)	43 HRC	156.1 (1076)	202.9 (1399)
Agbasie ike & nke dị ọkụ 550°F (288°C)	40 HRC	148.3 (1022)	187.0 (1289)
Agbasie ike & nke dị ọkụ 600°F (316°C)	40 HRC	148.8 (1026)	186.1 (1283)
Agbasie ike & nke dị ọkụ 800°F (427°C)	41 HRC	132.9 (916)	188.5 (1300)
Agbasie ike & Ọkụ 900°F (482°C)	41 HRC	122.6 (845)	154.3 (1063)
1000ºF (538°C) siri ike	35 HRC	127.9 (882)	154.3 (1063)
Agbasie ike & nke dị ọkụ 1200°F (649°C)	98 HRB	85.5 (589)	111.2 (767)

Ngwa:

Ngwa ndị chọrọ nguzogide corrosion na-adịghị mma na akụrụngwa akụrụngwa dị elu dị mma maka Alloy 410HT. Ọmụmatụ nke ngwa na-ejikarị Alloy 410HT gụnyere:

• Ihe oriri
• Uzuoku na ikuku turbine
• Ngwa kichin
• Bolts, akụ, kposara
• Akụkụ mgbapụta na valvụ na ogwe osisi
• Akwa akwa ubube m
• Ngwa eze na nke ịwa ahụ
• Nozzles
• Bọọlụ nchara siri ike na oche maka nfuli olulu mmiri mmanụ