AISI 4140 ekivalan asye
| Peyi |
Lachin |
Japon |
Almay |
USA |
Britanik |
| Estanda |
GB/T 3077 |
JIS G4105 |
DIN (W-Nr.)
EN 10250 |
AISI/ASTM
ASTM A29 |
BS 970 |
| Klas |
42CrMo |
SCM440 |
42crmo4/1.7225 |
4140 |
EN19/709M40 |
Konpozisyon chimik asye AISI 4140
| Klas |
C |
Si |
Mn |
P |
S |
Kr |
Mo |
Ni |
| 42CrMo |
0.38-0.45 |
0.17-0.37 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.2 |
0.15-0.25 |
- |
| SCM440 |
0.38-0.43 |
0.15-0.35 |
0.6-0.85 |
≤0.035 |
≤0.04 |
0.9-1.2 |
0.15-0.30 |
- |
| 42crmo4/1.7225 |
0.38-0.45 |
≤ 0.4 |
0.6-0.9 |
≤0.025 |
≤0.035 |
0.9-1.2 |
0.15-0.30 |
- |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0.035 |
≤0.04 |
0.8-1.1 |
0.15-0.25 |
- |
| EN19/709M40 |
0.35-0.45 |
0.15-0.35 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.5 |
0.2-0.40 |
- |
Pwopriyete mekanik asye AISI 4140 (pou konsèy sèlman)
| Klas |
Fòs rupture
σb (MPa) |
Sede fòs
σs (MPa) |
Elongasyon
δ5 (%) |
Rediksyon
ψ (%) |
Valè enpak
Akv (J) |
Dite |
| 4140 |
≥1080 |
≥930 |
≥12 |
≥45 |
≥63 |
28-32HRC |
Apèsi sou asye AISI 4140
| Gwosè |
Round |
Dyamèt 6-1200mm |
| Plak/Plat/Blòk |
Epesè
6mm-500mm |
Lajè
20mm-1000mm |
| Tretman chalè |
Nòmalize; rkwit ; Trempe ; Tanpered |
| Kondisyon sifas |
Nwa; kale; Poli; Machined; Grinde; Vire; Milled |
| Kondisyon livrezon |
Fòje; Woule cho; Fwad trase |
| Tès |
Fòs rupture, fòs sede, elongasyon, zòn nan rediksyon, valè enpak, dite, gwosè grenn, tès ultrasons, enspeksyon US, tès patikil mayetik, elatriye. |
| Tèm peman |
T/T;L/C;/Lajan gram/ Paypal |
| Tèm komès |
FOB; CIF; C&F; elatriye.. |
| Tan livrezon |
30-45 jou |
| Aplikasyon |
AISI 4140 asye jwenn anpil aplikasyon kòm forgings pou endistri ayewospasyal, lwil oliv ak gaz, otomobil, agrikòl ak defans elatriye.
Aplikasyon tipik pou itilizasyon asye 4140 yo enkli: fòje angrenaj, file koton, enstalasyon, jig, kolye, aks, pati transporteur, ba kòk, pati antre, arbr, piyon, poto, pignon, arbr ponp, belye mouton, ak angrenaj bag elatriye. |
Pwopriyete Fizik
Pwopriyete fizik asye alyaj AISI 4140 yo make nan tablo ki anba la a.
| Pwopriyete |
Metrik |
Imperial |
| Dansite |
7.85 g/cm3 |
0.284 lb/in³ |
| Pwen k ap fonn |
1416 °C |
2580°F |
Pwopriyete mekanik
Tablo ki anba la a montre pwopriyete mekanik AISI 4140 asye alyaj.
| Pwopriyete |
Metrik |
Imperial |
| Fòs rupture |
655 MPa |
95000 psi |
| Sede fòs |
415 MPa |
60200 psi |
| Modil esansyèl (tipik pou asye) |
140 GPa |
20300 ksi |
| Modil Chea (tipik pou asye) |
80 GPa |
11600 ksi |
| Modil elastik |
190-210 GPa |
27557-30458 ksi |
| Rapò Poisson a |
0.27-0.30 |
0.27-0.30 |
| Elongasyon nan kraze (nan 50 mm) |
25.70% |
25.70% |
| Dite, Brinell |
197 |
197 |
| Dite, Knoop (konvèti soti nan dite Brinell) |
219 |
219 |
| Dite, Rockwell B (konvèti soti nan dite Brinell) |
92 |
92 |
| Dite, Rockwell C (konvèti soti nan dite Brinell. Valè pi ba pase nòmal HRC ranje, pou rezon konparezon sèlman) |
13 |
13 |
| Dite, Vickers (konvèti soti nan dite Brinell) |
207 |
207 |
| Machinability (ki baze sou AISI 1212 kòm 100 machinability) |
65 |
65 |
Pwopriyete tèmik
Pwopriyete tèmik asye alyaj AISI 4140 yo bay nan tablo ki anba la a.
| Pwopriyete |
Metrik |
Imperial |
| Koyefisyan ekspansyon tèmik (@ 0-100°C/32-212°F) |
12.2 µm/m°C |
6.78 µin/in°F |
| Konduktivite tèmik (@ 100°C) |
42.6 W/mK |
296 BTU nan/hr.ft².°F |
Lòt Deziyasyon
Lòt deziyasyon ki ekivalan a asye alyaj AISI 4140 yo ki nan lis nan tablo ki anba la a.
| AMS 6349 |
ASTM A193 (B7, B7M) |
ASTM A506 (4140) |
ASTM A752 (4140) |
| AMS 6381 |
ASTM A194 (7, 7M) |
ASTM A513 |
ASTM A829 |
| AMS 6382 |
ASTM A29 (4140) |
ASTM A513 (4140) |
SAE J1397 (4140) |
| AMS 6390 |
ASTM A320 (L7, L7M, L7D) |
ASTM A519 (4140) |
SAE J404 (4140) |
| AMS 6395 |
ASTM A322 (4140) |
ASTM A646 (4140) |
SAE J412 (4140) |
| AMS 6529 |
ASTM A331 (4140) |
ASTM A711 |
|
Faktori ak Tretman Chalè
Machinability
AISI 4140 alyaj asye gen bon machinability nan kondisyon an rkwit.
Fòme
AISI 4140 alyaj asye gen gwo duktilite. Li ka fòme lè l sèvi avèk teknik konvansyonèl nan kondisyon an rkwit. Li mande plis presyon oswa fòs pou fòme paske li pi di pase asye kabòn plenn.
Soude
AISI 4140 alyaj asye ka soude lè l sèvi avèk tout teknik konvansyonèl yo. Sepandan, pwopriyete yo mekanik nan asye sa a pral afekte si li soude nan kondisyon an chalè-trete, ak tretman chalè apre-soude yo ta dwe fèt.
Tretman Chalè
AISI 4140 alyaj asye chofe nan 845 ° C (1550 ° F) ki te swiv pa trempe nan lwil oliv. Anvan redi, li ka nòmalize pa chofe li nan 913 ° C (1675 ° F) pou yon peryòd tan ki long, ki te swiv pa refwadisman lè.
Fòje
AISI 4140 alyaj asye fòje nan 926 a 1205 ° C (1700 a 2200 ° F)
Travay cho
AISI 4140 asye alyaj ka cho travay nan 816 a 1038 ° C (1500 a 1900 ° F)
Travay Fwad
AISI 4140 alyaj asye ka frèt travay lè l sèvi avèk metòd konvansyonèl nan kondisyon an rkwit.
Recuit
AISI 4140 alyaj asye se rkwit nan 872 ° C (1600 ° F) ki te swiv pa tou dousman refwadisman nan gwo fou a.
Tanperaman
AISI 4140 alyaj asye ka apeze nan 205 a 649 ° C (400 a 1200 ° F) depann sou nivo dite vle a. Ka dite nan asye a ap ogmante si li gen yon tanperati ki pi ba tanperaman. Pou egzanp, yon fòs rupture nan 225 ksi ka reyalize pa tanperaman nan 316 ° C (600 ° F), ak fòs rupture nan 130 ksi ka reyalize pa tanperaman nan 538 ° C (1000 ° F).
Redi
AISI 4140 alyaj asye ka fè tèt di pa travay frèt, oswa chofaj ak trempe.