Q550NH Steel

Segondè tansyon dezagregasyon asye Q550NH posede fòs sede pi wo a 550 Mpa ak fòs rupture nan 620-780 Mpa. Pou amelyore pwopriyete asye, eleman alyaj sa yo ka ajoute chwazi, Nb 0.015-0.060%, V 0.02-0.12%, Ti 0.02-0.10. %,Alt min.0.020%.Nb+V+Ti max.0.22%.

Espesifikasyon yo:
Epesè: 3mm--150mm
Lajè: 30mm--4000mm
Longè: 1000mm--12000mm
Estanda: ASTM EN10025 JIS GB

Segondè tansyon dezagregasyon asye Q550NH, Q550NH asye plak, Q550NH corten plak posede fòs sede pi wo pase 550 Mpa ak fòs rupture nan 620-780 Mpa. Pou amelyore pwopriyete asye, eleman alyaj sa yo ka ajoute chwazi, Nb 0.015-0.060%, V 0.02 -0.12%, Ti 0.02-0.10%, Alt min.0.020%. Nb+V+Ti max.0.22%.

Pwopriyete mekanik pou Q550NH corten asye:

Epesè (mm)
Q550NH	≤ 16	> 16 ≤ 40	> 40 ≤ 60	>60
Fòs sede (≥Mpa)	550	540	530	530
Fòs rupture (Mpa)	620-780

Konpozisyon chimik pou Q550NH Corten asye (Analiz Chalè Max%)

Pwensipal eleman chimik konpozisyon Q550NH
C	Si	Mn	P	S	Cu	Ni	Kr
0.16	0.65	2.00	0.025	0.030	0.20-0.55	0.12-0.65	0.30-1.25

Kondisyon teknik ak sèvis adisyonèl pou plak asye Q550NH:
♦ Tès tansyon wo
♦ Ba tanperati enpak tès
♦ Simulation tretman chalè apre soude (PWHT)
♦ Li te bay sètifika tès orijinal Mill anba EN 10204 FÒMA 3.1/3.2
♦ Piki eksplozif ak penti, koupe ak soude dapre demann itilizatè fen a
♦ G101 Gid pou estime rezistans korozyon atmosferik nan asye alyaj ki ba