JIS-SMA400AW asye

Voye Imèl

Chat Kounye a

Lis pwodwi yo

Gnee asye, ekipman pou asye soti nan syèl la nan lanmè yo disponib, mondyal aksesib;

Steel tiyo

Tiyo asye san pwoblèm Alloy Steel Tiyo Kabòn Steel tiyo API liy tiyo Soude tiyo asye Galvanize tiyo asye Fittings

Asye pur

Nerjaveèi asye bobin / Fèy Tiyo asye pur Fittings

Plak asye

Tan ki reziste Steel Chodyè presyon veso Steel Plak asye konstriksyon bato Mete plak asye ki reziste Hight fòs Low Alloy Steel Kabòn asye Plak asye karo Alloy Steel Plak

H gwo bout bwa Ang Chèn Steel Round Bar

Steel galvanize

Galvanize bobin / Fèy Prepainted bobin asye Fèy twati corrugated

Metal aliminyòm

Automotive Steel

Kontakte nou

Imèl : sale@gneesteel.com

Mobile: +86 15824687445 kelly

Tel: +86 372-5055135

Adrès: No 4-1114,Beichen Building,Beicang Town,Beichen Distri Tianjin,Lachin.

Entwodiksyon pwodwi Done teknik

Entwodiksyon pwodwi

SMA400AW se yon asye ki reziste move tan ki te kreye pa alyaj kwiv, chromium ak nikèl. SMA400AW te ajoute fosfò ki fè materyèl la pi byen adapte pou aplikasyon pou gaz lafimen ak pou fasas ayestetik.
Lachin CNS SMA400AW Lachin Taiwan asye estriktirèl ak SMA400AW Pwopriyete mekanik, eleman chimik, referans kwa, Datasheet.
SMA400AW Detay Teknik:
Tretman Chalè: Nòmalize, Trempe, Tanperaman, HIC, Tès Enpak,. (Opsyonèl si yo pa bay règ yo)

Espesifikasyon yo:
Epesè: 3mm--150mm
Lajè: 30mm--4000mm
Longè: 1000mm--12000mm
Estanda: ASTM EN10025 JIS GB

Done teknik

JIS G3114 SMA400AW konpozisyon chimik ak pwopriyete mekanik:
Pwopriyete mekanik pou asye Corten SMA400AW:

Epesè (mm)
SMA400AW	≤ 16	> 16 ≤ 40	> 40 ≤ 75	> 75 ≤ 100	> 100 ≤ 160	> 160
Fòs sede (≥Mpa)	245	235	215	215	205	195
Fòs rupture (Mpa)	400-540

Konpozisyon chimik pou SMA400AW Corten asye (Analiz Louch Max%)

Pwensipal eleman chimik konpozisyon SMA400AW
C	Si	Mn	P	S	Cu	Kr	Ni
0.18	0.15-0.65	1.25	0.035	0.035	0.30-0.50	0.45-0.75	0.05-0.30

SMA400AW Lòt Kondisyon:
UT (Egzamen Ultrasonic), AR (Kòm woule cho sèlman), TMCP (Tèmik Pwosesis kontwòl mekanik), N (Normalized), Q + T (Tenn ak Tanperaman), Z Direksyon Tès (Z15, Z25, Z35), Charpy V- Egzamen Enpak Notch, tès HIC, NDT, PWHT (Simile Post Weld Chalè Tretman), NACE0175, Tès Twazyèm Pati (Tankou Tès SGS), kouvwi oswa piki eksplozif ak penti.

Gen rapò Kalite Steel

Kalite Steel	Estanda	Kòd peyi a	C (%)	V (%)	Si(%)	Mn(%)	P(%)	S(%)	Cr (%)	Ni (%)	Cu (%)
SMA400AW	4269	CNS	≦0.18		0.15-0.65	≦1.25	≦0.035	≦0.035	0.45-0.75	0.05-0.30	0.30-0.50
SMA400AW	G3114	JIS	≦0.18		0.15-0.65	≦1.25	≦0.035	≦0.035	0.45-0.75	0.05-0.30	0.30-0.50
A588Gr.C	A588	ASTM	≦0.15	0.01-0.10	0.15-0.40	0.80-1.35	≦0.04	≦0.05	0.30-0.50	0.25-0.50	0.20-0.50

Kalite Steel	Sede estrès (Mpa)	Tensile estrès (Mpa)	elongasyon (%)	Epè (mm)
SMA400AW	≧245	400-540	≧23	≦16
SMA400AW	≧245	400-540	≧23	≦16
A588Gr.C	≧345	≧485		≦101.6