Konpozisyon chimik ak pwopriyete mekanik:
ASTM A537 klas 3 (A537CL3)
| MATERYÈL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 klas 3 (A537CL3) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERYÈL |
Fòs rupture (MPa) |
Sede fòs(MPa) MIN |
% elongasyon MIN |
| ASTM A537 klas 3 (A537CL3) |
485-690 |
275-380 |
20 |
ASTM A537 klas 2 (A537CL2)
| MATERYÈL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 klas 2 (A537CL2) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERYÈL |
Fòs rupture (MPa) |
Sede fòs(MPa) MIN |
% elongasyon MIN |
| ASTM A537 klas 2 (A537CL2) |
485-690 |
315-415 |
20 |
ASTM A537 klas 1 (A537CL1)
| MATERYÈL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 klas 1 (A537CL1) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERYÈL |
Fòs rupture (MPa) |
Sede fòs(MPa) MIN |
% elongasyon MIN |
| ASTM A537 klas 1 (A537CL1) |
450-585 |
310 |
18 |
Dokiman referans yo
Estanda ASTM:
A20/A20M: Spesifikasyon pou Kondisyon Jeneral pou Plak Veso Presyon
A435/A435: Pou Egzamen ultrasons dwat-gwo bout bwa nan plak asye
A577/A577M: Pou Egzamen ang-gwo bout bwa ultrasons nan plak asye
A578/A578M: Pou Egzamen Dwat-gwo bout bwa ultrasons nan plak asye woule pou aplikasyon espesyal
Nòt fabrikasyon:
Plak asye anba ASTM A537 Klas 1, 2 ak 3 yo dwe touye asye epi konfòme yo avèk egzijans gwosè amann austenitic nan Spesifikasyon A20/A20M.
Metòd tretman chalè:
Tout plak anba ASTM A537 yo dwe trete chalè jan sa a:
Plak ASTM A537 Klas 1 yo dwe nòmalize.
Plak klas 2 ak klas 3 yo dwe etenn ak tanperaman. Tanperati tanperaman an pou plak Klas 2 pa dwe mwens pase 1100 ° F [595 ° C] epi pa dwe mwens pase 1150 ° F [620 ° C] pou plak Klas 3.