Co-dhèanamh ceimigeach stàilinn AISI 4140
| Ìre |
c |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
| 42CrMo |
0.38-0.45 |
0.17-0.37 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.2 |
0.15-0.25 |
- |
| SCM440 |
0.38-0.43 |
0.15-0.35 |
0.6-0.85 |
≤0.035 |
≤0.04 |
0.9-1.2 |
0.15-0.30 |
- |
| 42crmo4/1.7225 |
0.38-0.45 |
≤ 0.4 |
0.6-0.9 |
≤0.025 |
≤0.035 |
0.9-1.2 |
0.15-0.30 |
- |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0.035 |
≤0.04 |
0.8-1.1 |
0.15-0.25 |
- |
| EN19 /709M40 |
0.35-0.45 |
0.15-0.35 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.5 |
0.2-0.40 |
- |
Togalaichean meacanaigeach stàilinn AISI 4140 (airson stiùireadh a-mhàin)
| Ìre |
Neart tensile
σb(MPa) |
Neart toraidh
σs (MPa) |
Leudachadh
δ5 (%) |
Lùghdachadh
ψ (%) |
Luach Buaidh
Akv (J) |
cruas |
| 4140 |
≥1080 |
≥930 |
≥12 |
≥45 |
≥63 |
28-32HRC |
Sealladh farsaing air stàilinn AISI 4140
| Meud |
Cruinn |
Dia 6-1200mm |
| Plate / Flat / Bloc |
Tigheadas
6mm-500mm |
Leud
20mm-1000mm |
| Làimhseachadh teas |
Normalaichte; Annal; Air a chuartachadh; Tempered |
| Suidheachadh uachdar |
Dubh; Peeled; Snasail; Inneal; Air a bhleith; Thionndaidh; Milled |
| Suidheachadh lìbhrigidh |
Fasgadh; Hot roiligeadh; Fuar air a tharraing |
| Deuchainn |
Neart tensile, Neart toraidh, leudachadh, raon lughdachadh, luach buaidh, cruas, meud gràin, deuchainn ultrasonic, sgrùdadh na SA, deuchainn mìrean magnetach, msaa. |
| Teirmean pàighidh |
T / T; L / C; / Money gram / Paypal |
| Teirmean malairt |
FOB; CIF; C&F; msaa. |
| Ùine lìbhrigidh |
30-45 làithean |
| Iarrtas |
Bidh stàilinn AISI 4140 a’ lorg mòran thagraidhean mar gheàrdan airson na gnìomhachasan aerospace, ola is gas, càraichean, àiteachas agus dìon msaa.
Tha tagraidhean àbhaisteach airson 4140 cleachdadh stàilinn a’ toirt a-steach: gèaraichean cruthaichte, dealgan, tàmh-àirneisean, jigs, collars, Axles, pàirtean giùlain, bàraichean feannag, pàirtean logaidh, shafts, sprockets, studs, pinions, pump shafts, reitheachan, agus gèaraichean fàinne msaa. |
Feartan corporra
Tha feartan fiosaigeach AISI 4140 alloy stàilinn air an comharrachadh sa chlàr a leanas.
| Feartan |
Meadrach |
ìmpireil |
| Dùmhlachd |
7.85 g /cm3 |
0.284 lb /in³ |
| Puing leaghaidh |
1416°C |
2580°F |
Feartan meacanaigeach
Tha an clàr a leanas a’ mìneachadh feartan meacanaigeach AISI 4140 alloy stàilinn.
| Feartan |
Meadrach |
ìmpireil |
| Neart tensile |
655 mpa |
95 000 psi |
| Neart toraidh |
415 mpa |
60 200 psi |
| Modulus mòr (àbhaisteach airson stàilinn) |
140 GPa |
20300 mìle |
| Modulus rùsgaidh (àbhaisteach airson stàilinn) |
80 GPa |
11600 ksi |
| Modal elastic |
190-210 GPa |
27557-30458 ksi |
| Co-mheas Poisson |
0.27-0.30 |
0.27-0.30 |
| Leudachadh aig àm briseadh (ann an 50 mm) |
25.70% |
25.70% |
| Cruaidh, Brinell |
197 |
197 |
| Cruas, Knoop (air a thionndadh bho chruas Brinell) |
219 |
219 |
| Cruas, Rockwell B (air a thionndadh bho chruas Brinell) |
92 |
92 |
| Cruas, Rockwell C (air a thionndadh bho chruas Brinell. Luach nas ìsle na raon àbhaisteach HRC, airson adhbharan coimeas a-mhàin) |
13 |
13 |
| Cruas, Vickers (air a thionndadh bho chruas Brinell) |
207 |
207 |
| Machinability (stèidhichte air AISI 1212 mar 100 machinability) |
65 |
65 |
Feartan teirmeach
Tha feartan teirmeach stàilinn alloy AISI 4140 air an toirt seachad sa chlàr a leanas.
| Feartan |
Meadrach |
ìmpireil |
| Co-èifeachd leudachaidh teirmeach (@ 0-100 ° C / 32-212 ° F) |
12.2 µm /m ° C |
6.78 µin /ann °F |
| giùlan teirmeach (@ 100 ° C) |
42.6 W /mK |
296 BTU ann an /hr.ft².°F |
Sònrachaidhean Eile
Tha sònrachaidhean eile co-ionann ri AISI 4140 alloy stàilinn air an liostadh sa chlàr a leanas.
| AMS 6349 |
ASTM A193 (B7, B7M) |
ASTM A506 (4140) |
ASTM A752 (4140) |
| AMS 6381 |
ASTM A194 (7, 7M) |
ASTM A513 |
ASTM A829 |
| AMS 6382 |
ASTM A29 (4140) |
ASTM A513 (4140) |
SAE J1397 (4140) |
| AMS 6390 |
ASTM A320 (L7, L7M, L7D) |
ASTM A519 (4140) |
SAE J404 (4140) |
| AMS 6395 |
ASTM A322 (4140) |
ASTM A646 (4140) |
SAE J412 (4140) |
| AMS 6529 |
ASTM A331 (4140) |
ASTM A711 |
|
Dèanamh agus Làimhseachadh Teas
Machinability
Tha innealachadh math aig stàilinn alloy AISI 4140 anns an t-suidheachadh annealed.
A' cruthachadh
Tha sùbailteachd àrd aig stàilinn alloy AISI 4140. Faodar a chruthachadh a 'cleachdadh dhòighean àbhaisteach ann an staid annealed. Feumaidh e barrachd cuideam no feachd airson a bhith a 'cruthachadh oir tha e nas cruaidhe na steels gualain sìmplidh.
Tàthadh
Faodar stàilinn alloy AISI 4140 a thàthadh a’ cleachdadh a h-uile dòigh àbhaisteach. Ach, bidh buaidh air feartan meacanaigeach an stàilinn seo ma thèid a thàthadh ann an staid teas-làimhseachaidh, agus bu chòir làimhseachadh teas an dèidh tàthaidh a dhèanamh.
Làimhseachadh teas
Tha stàilinn alloy AISI 4140 air a theasachadh aig 845 ° C (1550 ° F) agus an uairsin a’ cuir às ann an ola. Mus cruadhaich e, faodar a dhèanamh àbhaisteach le bhith ga theasachadh aig 913 ° C (1675 ° F) airson ùine mhòr, agus an uairsin fuarachadh èadhair.
Cruthachadh
Tha stàilinn alloy AISI 4140 air a chruthachadh aig 926 gu 1205 ° C (1700 gu 2200 ° F)
Obair theth
Faodar stàilinn alloy AISI 4140 obrachadh gu teth aig 816 gu 1038 ° C (1500 gu 1900 ° F)
Obair Fuar
Faodar stàilinn alloy AISI 4140 a bhith air obrachadh gu fuar le bhith a’ cleachdadh dhòighean àbhaisteach anns an t-suidheachadh annealed.
Annealing
Tha stàilinn alloy AISI 4140 air a cheangal aig 872 ° C (1600 ° F) agus an uairsin fuarachadh gu slaodach san fhùirneis.
Tempering
Faodar stàilinn alloy AISI 4140 a theannachadh aig 205 gu 649 ° C (400 gu 1200 ° F) a rèir an ìre cruas a tha thu ag iarraidh. Faodar cruas na stàilinn àrdachadh ma tha teòthachd teothachd nas ìsle aige. Mar eisimpleir, faodar neart tensile de 225 ksi a choileanadh le bhith a’ teannachadh aig 316 ° C (600 ° F), agus faodar neart tensile de 130 ksi a choileanadh le bhith a’ teannachadh aig 538 ° C (1000 ° F).
Cruadhachadh
Faodar stàilinn alloy AISI 4140 a chruadhachadh le bhith ag obair fuar, no le bhith a’ teasachadh agus a’ cuir às.