AISI 4140 Stiel lykweardich
| Lân |
Sina |
Japan |
Dútslân |
USA |
Britsk |
| Standert |
GB/T 3077 |
JIS G4105 |
DIN (W-Nr.)
EN 10250 |
AISI/ASTM
ASTM A29 |
BS 970 |
| Klasse |
42 CrMo |
SCM440 |
42crmo4/1.7225 |
4140 |
EN19/709M40 |
AISI 4140 stiel gemyske gearstalling
| Klasse |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
| 42 CrMo |
0.38-0.45 |
0.17-0.37 |
0.5-0.80 |
≤0,035 |
≤0,035 |
0.9-1.2 |
0.15-0.25 |
- |
| SCM440 |
0.38-0.43 |
0.15-0.35 |
0.6-0.85 |
≤0,035 |
≤0,04 |
0.9-1.2 |
0.15-0.30 |
- |
| 42crmo4/1.7225 |
0.38-0.45 |
≤ 0,4 |
0.6-0.9 |
≤0,025 |
≤0,035 |
0.9-1.2 |
0.15-0.30 |
- |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0,035 |
≤0,04 |
0.8-1.1 |
0,15-0,25 |
- |
| EN19/709M40 |
0.35-0.45 |
0.15-0.35 |
0.5-0.80 |
≤0,035 |
≤0,035 |
0.9-1.5 |
0.2-0.40 |
- |
AISI 4140 stiel meganyske eigenskippen (allinich foar begelieding)
| Klasse |
Treksterkte
σb(MPa) |
Yield sterkte
σs (MPa) |
Ferlinging
δ5 (%) |
Ferleging
ψ (%) |
Impact Wearde
Akv (J) |
Hurdens |
| 4140 |
≥1080 |
≥930 |
≥12 |
≥45 |
≥63 |
28-32 HRC |
AISI 4140 stiel oersjoch
| Grutte |
Rûn |
Dia 6-1200 mm |
| Plaat/Flat/Blok |
Dikte
6mm-500mm |
Breedte
20mm-1000mm |
| Waarmte behanneling |
normalisearre; Annealed haadwurd ; Quenched ; Tempered |
| Surface condition |
Swart; Peeled; Oppoetst; machined; grinded; Turned; Milled |
| Levering betingst |
Forged; waarm rôle; Kâld tekene |
| Toets |
Treksterkte, opbringststerkte, ferlinging, gebiet fan reduksje, ynfloedwearde, hurdens, korrelgrutte, ultrasone test, US-ynspeksje, magnetyske dieltsje testen, ensfh. |
| Betellingsbetingsten |
T/T;L/C;/Money gram/ Paypal |
| Hannelsbetingsten |
FOB; CIF; C&F; ensfh. |
| Levertiid |
30-45 dagen |
| Oanfraach |
AISI 4140 stiel fynt in protte tapassingen as smeedijen foar de loftfeart, oalje en gas, automotive, agraryske en definsje yndustry ensfh.
Typyske tapassingen foar 4140 stielgebrûk omfetsje: smeid gears, spindels, fixtures, jigs, kragen, assen, transportbanddielen, kraaibalken, houtdielen, assen, kettingwielen, studs, pinions, pompassen, rammen, en ringgears ensfh. |
Fysike eigenskippen
De fysike eigenskippen fan AISI 4140 alloy stiel wurde markearre yn de folgjende tabel.
| Eigenskippen |
Metric |
Keizerlik |
| Tichtheid |
7,85 g/cm3 |
0.284 lb/yn³ |
| Smeltpunt |
1416°C |
2580°F |
Meganyske eigenskippen
De folgjende tabel sketst de meganyske eigenskippen fan AISI 4140 alloy stiel.
| Eigenskippen |
Metric |
Keizerlik |
| Treksterkte |
655 MPa |
95000 psi |
| Yield sterkte |
415 MPa |
60200 psi |
| Bulk modulus (typysk foar stiel) |
140 GPa |
20300 ksi |
| Shear modulus (typysk foar stiel) |
80 gpa |
11600 ksi |
| Elastyske modulus |
190-210 GPa |
27557-30458 ksi |
| Poisson syn ratio |
0.27-0.30 |
0.27-0.30 |
| Breekrek (in 50 mm) |
25.70% |
25.70% |
| Hardheid, Brinell |
197 |
197 |
| Hardheid, Knoop (omset fan Brinell hurdens) |
219 |
219 |
| Hardness, Rockwell B (omset fan Brinell hurdens) |
92 |
92 |
| Hardness, Rockwell C (omboud út Brinell hurdens. Wearde ûnder normale HRC berik, allinnich foar ferliking doelen) |
13 |
13 |
| Hardheid, Vickers (omset fan Brinell hurdens) |
207 |
207 |
| Bewurkberens (basearre op AISI 1212 as 100 bewurkberens) |
65 |
65 |
Termyske eigenskippen
De termyske eigenskippen fan AISI 4140 alloy stiel wurde jûn yn de folgjende tabel.
| Eigenskippen |
Metric |
Keizerlik |
| Termyske útwreidingskoëffisjint (@0-100 °C/32-212 °F) |
12,2 µm/m°C |
6.78 µin/in°F |
| Thermyske konduktiviteit (@ 100 °C) |
42.6 W/mK |
296 BTU yn/hr.ft².°F |
Oare oantsjuttings
Oare oantsjuttings lykweardich oan AISI 4140 alloy stiel wurde neamd yn de folgjende tabel.
| AMS 6349 |
ASTM A193 (B7, B7M) |
ASTM A506 (4140) |
ASTM A752 (4140) |
| AMS 6381 |
ASTM A194 (7, 7M) |
ASTM A513 |
ASTM A829 |
| AMS 6382 |
ASTM A29 (4140) |
ASTM A513 (4140) |
SAE J1397 (4140) |
| AMS 6390 |
ASTM A320 (L7, L7M, L7D) |
ASTM A519 (4140) |
SAE J404 (4140) |
| AMS 6395 |
ASTM A322 (4140) |
ASTM A646 (4140) |
SAE J412 (4140) |
| AMS 6529 |
ASTM A331 (4140) |
ASTM A711 |
|
Fabrication en waarmte behanneling
Bewurkberens
AISI 4140 alloy stiel hat goede machinability yn de annealed steat.
Formearje
AISI 4140 alloy stiel hat hege ductility. It kin wurde foarme mei konvinsjonele techniken yn 'e annealed tastân. It fereasket mear druk as krêft foar it foarmjen, om't it hurder is dan gewoane koalstofstiel.
Welding
AISI 4140 alloy stiel kin wurde laske mei alle konvinsjonele techniken. De meganyske eigenskippen fan dit stiel sille lykwols wurde beynfloede as it wurdt laske yn 'e waarmte-behannele tastân, en post-weld-waarmebehanneling moat wurde útfierd.
Waarmte behanneling
AISI 4140 alloy stiel wurdt ferwaarme op 845 ° C (1550 ° F) folge troch quenching yn oalje. Foar it ferhurden kin it normalisearre wurde troch it foar in lange perioade te ferwaarmjen op 913 ° C (1675 ° F), folge troch loftkoeling.
Smeden
AISI 4140 alloy stiel wurdt smeid by 926 oant 1205 ° C (1700 oant 2200 ° F)
Hot Working
AISI 4140 alloy stiel kin hjit bewurke wurde op 816 oant 1038 ° C (1500 oant 1900 ° F)
Kâld wurkjen
AISI 4140 alloy stiel kin kâld wurke mei help fan konvinsjonele metoaden yn de annealed tastân.
Annealing
AISI 4140 alloy stiel wurdt annealed by 872 ° C (1600 ° F) folge troch stadich koeling yn 'e oven.
Tempering
AISI 4140 alloy stiel kin tempered op 205 oant 649 ° C (400 oant 1200 ° F) ôfhinklik fan it winske hurdens nivo. De hurdens fan it stiel kin ferhege wurde as it in legere temperatuertemperatuer hat. Bygelyks, in treksterkte fan 225 ksi kin berikt wurde troch temperearjen by 316 ° C (600 ° F), en treksterkte fan 130 ksi kin berikt wurde troch temperearjen by 538 ° C (1000 ° F).
Ferharding
AISI 4140 alloy stiel kin ferhurde wurde troch kâld wurkjen, of ferwaarming en quenching.
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)
.jpg)