Gemyske gearstalling en meganyske eigenskippen:
ASTM A537 Klasse 3 (A537CL3)
| MATERIAAL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Klasse 3 (A537CL3) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERIAAL |
Tensile Strength (MPa) |
Yield Strength (MPa) MIN |
% Ferlinging MIN |
| ASTM A537 Klasse 3 (A537CL3) |
485-690 |
275-380 |
20 |
ASTM A537 Klasse 2 (A537CL2)
| MATERIAAL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Klasse 2 (A537CL2) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERIAAL |
Tensile Strength (MPa) |
Yield Strength (MPa) MIN |
% Ferlinging MIN |
| ASTM A537 Klasse 2 (A537CL2) |
485-690 |
315-415 |
20 |
ASTM A537 Klasse 1 (A537CL1)
| MATERIAAL |
C |
Mn |
Si |
P≤ |
S≤ |
| ASTM A537 Klasse 1 (A537CL1) |
0.24 |
0.13-0.55 |
0.92-1.72 |
0.035 |
0.035 |
| MATERIAAL |
Tensile Strength (MPa) |
Yield Strength (MPa) MIN |
% Ferlinging MIN |
| ASTM A537 Klasse 1 (A537CL1) |
450-585 |
310 |
18 |
Ferwiisde dokuminten
ASTM noarmen:
A20 / A20M: Spesifikaasje foar Algemiene easken foar drukferfierplaten
A435/A435: Foar Straight-beam ultrasone ûndersyk fan stielen plaat
A577/A577M: Foar ultrasone hoekstraalûndersyk fan stielen platen
A578/A578M: Foar Straight-beam ultrasone ûndersiik fan rôle stielplaten foar spesjale tapassingen
Produksjenotysjes:
Stielplaat ûnder ASTM A537 Klasse 1, 2 en 3 sil wurde fermoarde stiel en foldogge oan fyn austenitic nôtgrutte eask fan spesifikaasje A20/A20M.
Metoaden foar waarmtebehanneling:
Alle platen ûnder ASTM A537 moatte wurde waarmte behannele as folget:
ASTM A537 Klasse 1 platen moatte wurde normalisearre.
Klasse 2 en Klasse 3 platen moatte wurde doft en temperearre. De temperatuertemperatuer foar Klasse 2-platen moat net minder wêze as 1100 °F [595 °C] en net minder dan 1150 °F [620 °C] foar Klasse 3-platen.