cyfansoddiad cemegol dur AISI 4140
| Gradd |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
| 42CrMo |
0.38-0.45 |
0.17-0.37 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.2 |
0.15-0.25 |
- |
| SCM440 |
0.38-0.43 |
0.15-0.35 |
0.6-0.85 |
≤0.035 |
≤0.04 |
0.9-1.2 |
0.15-0.30 |
- |
| 42crmo4/1.7225 |
0.38-0.45 |
≤ 0.4 |
0.6-0.9 |
≤0.025 |
≤0.035 |
0.9-1.2 |
0.15-0.30 |
- |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0.035 |
≤0.04 |
0.8-1.1 |
0.15-0.25 |
- |
| EN19 /709M40 |
0.35-0.45 |
0.15-0.35 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.5 |
0.2-0.40 |
- |
Priodweddau mecanyddol dur AISI 4140 (ar gyfer arweiniad yn unig)
| Gradd |
Cryfder tynnol
σb(MPa) |
Cryfder cynnyrch
σs (MPa) |
Elongation
δ5 (%) |
Gostyngiad
ψ (%) |
Gwerth Effaith
Akv (J) |
Caledwch |
| 4140 |
≥1080 |
≥930 |
≥12 |
≥45 |
≥63 |
28-32HRC |
Trosolygon dur AISI 4140
| Maint |
Rownd |
Dia 6-1200mm |
| Plât /Fflat / Bloc |
Trwch
6mm-500mm |
Lled
20mm-1000mm |
| Triniaeth wres |
Wedi'i normaleiddio; Annealed; Wedi torri; tymherus |
| Cyflwr wyneb |
Du; Peeled; sgleinio; Wedi'u peiriannu; Wedi'i falu; Trodd; Melino |
| Amod danfon |
Ffugio; Rholio poeth; Wedi'i dynnu'n oer |
| Prawf |
Cryfder tynnol, Cryfder cynnyrch, ehangiad, ardal o ostyngiad, gwerth effaith, caledwch, maint grawn, prawf ultrasonic, arolygiad yr Unol Daleithiau, profi gronynnau magnetig, ac ati. |
| Telerau talu |
T / T; L / C; / Money gram / Paypal |
| Telerau masnach |
FOB; CIF; C&F; etc. |
| Amser dosbarthu |
30-45 diwrnod |
| Cais |
Mae dur AISI 4140 yn dod o hyd i lawer o gymwysiadau fel gofaniadau ar gyfer y diwydiannau awyrofod, olew a nwy, modurol, amaethyddol ac amddiffyn ac ati.
Mae cymwysiadau nodweddiadol ar gyfer 4140 o ddefnyddiau dur yn cynnwys: gerau ffug, gwerthydau, gosodiadau, jigiau, coleri, Echelau, rhannau cludo, bariau brân, rhannau logio, siafftiau, sprocedi, stydiau, pinions, siafftiau pwmp, hyrddod, a gerau cylch ac ati. |
Priodweddau Corfforol
Amlygir priodweddau ffisegol dur aloi AISI 4140 yn y tabl canlynol.
| Priodweddau |
Metrig |
Ymerodrol |
| Dwysedd |
7.85 g /cm3 |
0.284 pwys / mewn³ |
| Pwynt toddi |
1416°C |
2580°F |
Priodweddau Mecanyddol
Mae'r tabl canlynol yn amlinellu priodweddau mecanyddol dur aloi AISI 4140.
| Priodweddau |
Metrig |
Ymerodrol |
| Cryfder tynnol |
655 MPa |
95000 psi |
| Cryfder cynnyrch |
415 MPa |
60200 psi |
| Modwlws swmp (nodweddiadol ar gyfer dur) |
140 GPa |
20300 ksi |
| Modwlws cneifio (nodweddiadol ar gyfer dur) |
80 GPa |
11600 ksi |
| Modwlws elastig |
190-210 GPa |
27557-30458 ksi |
| Cymhareb Poisson |
0.27-0.30 |
0.27-0.30 |
| Elongation ar egwyl (mewn 50 mm) |
25.70% |
25.70% |
| Caledwch, Brinell |
197 |
197 |
| Caledwch, Knoop (wedi'i drosi o galedwch Brinell) |
219 |
219 |
| Caledwch, Rockwell B (wedi'i drosi o galedwch Brinell) |
92 |
92 |
| Caledwch, Rockwell C (wedi'i drosi o galedwch Brinell. Gwerth yn is na'r ystod HRC arferol, at ddibenion cymharu yn unig) |
13 |
13 |
| Caledwch, Vickers (wedi'i drosi o galedwch Brinell) |
207 |
207 |
| Peiriannu (yn seiliedig ar AISI 1212 fel 100 machinability) |
65 |
65 |
Priodweddau Thermol
Rhoddir priodweddau thermol dur aloi AISI 4140 yn y tabl canlynol.
| Priodweddau |
Metrig |
Ymerodrol |
| Cyfernod ehangu thermol (@ 0-100 ° C / 32-212 ° F) |
12.2 µm /m°C |
6.78 µmewn /mewn°F |
| Dargludedd thermol (@ 100 ° C) |
42.6 W /mK |
296 BTU mewn /awr.ft².°F |
Dynodiadau Eraill
Rhestrir dynodiadau eraill sy'n cyfateb i ddur aloi AISI 4140 yn y tabl canlynol.
| AMS 6349 |
ASTM A193 (B7, B7M) |
ASTM A506 (4140) |
ASTM A752 (4140) |
| AMS 6381 |
ASTM A194 (7, 7M) |
ASTM A513 |
ASTM A829 |
| AMS 6382 |
ASTM A29 (4140) |
ASTM A513 (4140) |
SAE J1397 (4140) |
| AMS 6390 |
ASTM A320 (L7, L7M, L7D) |
ASTM A519 (4140) |
SAE J404 (4140) |
| AMS 6395 |
ASTM A322 (4140) |
ASTM A646 (4140) |
SAE J412 (4140) |
| AMS 6529 |
ASTM A331 (4140) |
ASTM A711 |
|
Gwneuthuriad a Thriniaeth Gwres
Machinability
Mae dur aloi AISI 4140 machinability da yn y cyflwr annealed.
Ffurfio
Mae gan ddur aloi AISI 4140 hydwythedd uchel. Gellir ei ffurfio gan ddefnyddio technegau confensiynol yn y cyflwr annealed. Mae angen mwy o bwysau neu rym ar gyfer ffurfio oherwydd ei fod yn llymach na dur carbon plaen.
Weldio
Gellir weldio dur aloi AISI 4140 gan ddefnyddio'r holl dechnegau confensiynol. Fodd bynnag, bydd priodweddau mecanyddol y dur hwn yn cael eu heffeithio os caiff ei weldio yn y cyflwr trin â gwres, a dylid perfformio triniaeth wres ôl-weldio.
Triniaeth Gwres
Mae dur aloi AISI 4140 yn cael ei gynhesu ar 845 ° C (1550 ° F) ac yna diffodd mewn olew. Cyn caledu, gellir ei normaleiddio trwy ei gynhesu ar 913 ° C (1675 ° F) am gyfnod hir, ac yna oeri aer.
gofannu
Mae dur aloi AISI 4140 wedi'i ffugio ar 926 i 1205 ° C (1700 i 2200 ° F)
Gweithio Poeth
Gellir gweithio'n boeth ar ddur aloi AISI 4140 ar 816 i 1038 ° C (1500 i 1900 ° F)
Gweithio Oer
Gall dur aloi AISI 4140 gael ei weithio'n oer gan ddefnyddio dulliau confensiynol yn y cyflwr anelio.
Anelio
Mae dur aloi AISI 4140 yn cael ei anelio ar 872 ° C (1600 ° F) ac yna oeri'n araf yn y ffwrnais.
tymheru
Gellir tymheru dur aloi AISI 4140 ar 205 i 649 ° C (400 i 1200 ° F) yn dibynnu ar y lefel caledwch a ddymunir. Gellir cynyddu caledwch y dur os oes ganddo dymheredd tymheru is. Er enghraifft, gellir cyflawni cryfder tynnol o 225 ksi trwy dymheru ar 316 ° C (600 ° F), a gellir cyflawni cryfder tynnol o 130 ksi trwy dymheru ar 538 ° C (1000 ° F).
Caledu
Gellir caledu dur aloi AISI 4140 trwy weithio oer, neu wresogi a diffodd.