Tiwbiau Boeler Di-dor ASTM A213 T22

Mae T22 Alloy Steel Tube (SA213 T22, Chorme-Moly) yn Tube Dur Alloy ferritig cyson ar gyfer gweinyddu tymheredd uchel. Mae'r deunydd T22 hwn gan gynnwys Tiwb Di-dor SA213 T22 a Tube Alloy Steel T22 yn briodol ar gyfer cymhwyso tymheredd uchel, er enghraifft, bwa, flanging (vanstoning), a thasgau fframio tebyg, ac ar gyfer weldio cyfuniad yn y busnes pŵer a phlanhigion petro-cyfansawdd.

Safon Weithredol		ASTM A213
Defnyddiau		T2, T5, T5b, T5c, T9, T11, T12, T17, T21, T22, T23, T24, T36,T91, T92, T122, T911
Maint	Diamedr Allanol	12.7 mm - 114.3 mm
	Trwch wal	0.8mm -15mm
	Hyd	Hyd hap sengl / Hyd hap dwbl 5m-14m, 5.8m, 6m, 10m-12m, 12m neu fel cais gwirioneddol y cwsmer
Diwedd		Pen plaen / Wedi'i beveled, wedi'i amddiffyn gan gapiau plastig ar y ddau ben, cwarts wedi'i dorri, rhigol, edafedd a chyplu, ac ati
Triniaeth Wyneb		Moel, Peintio du, farneisio, galfanedig, gwrth-cyrydiad Cotio 3PE PP /EP / FBE
Dulliau Technegol		Wedi'i dynnu'n oer /Ehangu'n boeth
Dulliau Profi		Profion cyfredol Eddy, profion hydrostatig neu archwiliad uwchsonig, NDT a hefyd gydag archwiliad eiddo cemegol a ffisegol
Pecynnu		Pibellau bach mewn bwndeli gyda stribedi dur cryf, mawr mewn darnau rhydd; Wedi'i orchuddio â bagiau gwehyddu plastig; Yn addas ar gyfer gweithrediad codi; Wedi'i lwytho mewn cynhwysydd 40 troedfedd neu 20 troedfedd neu mewn swmp Hefyd yn unol â cheisiadau cwsmeriaid
Cais		boeler, superheater, a thiwbiau cyfnewid gwres
Tystysgrifau		API ISO PED
Arolygiad Trydydd Parti		SGS BV TUV ac ati.

Gradd	C	Mn	P≤	S≤	Si	Cr	Mo	V≥
T11	0.05-0.15	0.30-0.60	0.025	0.025	0.50-1.00	0.50-1.00	1.00-1.50
T12	0.05-0.15	0.30-0.61	0.025	0.025	≤0.50	0.80-1.25	0.44-0.65
T13	0.05-0.15	0.30-0.60	0.025	0.025	≤0.50	1.90-2.60	0.87-1.13
T2	0.10-0.20	0.30-0.61	0.025	0.025	0.10-0.30	0.50-0.81	0.44-0.65
T5	≤0.15	0.30-0.60	0.025	0.025	≤0.50	4.00-6.00	0.45-0.65
T5b	≤0.15	0.30-0.60	0.025	0.025	1.00-2.00	4.00-6.00	0.45-0.65
T5c	≤0.12	0.30-0.60	0.025	0.025	≤0.50	4.00-6.00	0.45-0.65
T9	≤0.15	0.30-0.60	0.025	0.025	0.25-1.00	8.00-10.00	0.9-1.0
T22	0.05-0.15	0.30-0.60	0.025	0.025	≤0.50	1.90-2.60	0.87-1.13
T91	0.08-0.12	0.30-0.60	0.020	0.010	≤0.50	8-9.50	0.85-1.05	0.18-0.25
T92	0.07-0.13	0.30-0.60	0.020	0.010	≤0.50	8-9.50	0.3-0.60	0.15-0.25
T21	0.05-0.15	0.30-0.60	0.025	0.025	≤0.50	2.65-3.35	0.80-1.06

Safonol	Gradd dur	tynnol(MPa)	Cynnyrch (MPa)	Elongate(%)	Caledu
20MnG	20MnG	≥415	≥240	≥22
25MnG	25MnG	≥485	≥275	≥20
15CrMoG	15CrMoG	440～640	≥235	≥21
12Cr2MoG	12Cr2MoG	450～600	≥280	≥20
12Cr1MoVG	12Cr1MoVG	470～640	≥255	≥21
12Cr2MoWVTiB	12Cr2MoWVTiB	540～735	≥345	≥18
10Cr9Mo1VNb	10Cr9Mo1VNb	≥585	≥415	≥20
ASME SA210	SA210A-1	≥415	≥255	≥30	≤143HB
SA210C	SA210C	≥485	≥275	≥30	≤179HB
ASME SA213	SA213 T11	≥415	≥205	≥30	≤163HB
SA213 T12	SA213 T12	≥415	≥220	≥30	≤163HB
SA213 T22	SA213 T22	≥415	≥205	≥30	≤163HB
SA213 T23	SA213 T23	≥510	≥400	≥20	≤220HB
SA213 T91	SA213 T91	≥585	≥415	≥20	≤250HB
SA213 T92	SA213 T92	≥620	≥440	≥20	≤250HB
DIN17175	ST45.8/Ⅲ	410～530	≥255	≥21	/
15Mo3	15Mo3	450～600	≥270	≥22
13CrMo44	13CrMo44	440～590	≥290	≥22
10CrMo910	10CrMo910	480～630	≥280	≥20

OD	ynghyd â goddefgarwch (+)	Llai goddefgarwch (-)
10.29—48.3	0.4	0.4
<48.3—-≤114.3	0.79	0.79
<114.3—≤219.1	1.59	0.79
<219.1—≤323.9	2.38	0.79
<323.9	±1%